Anti-aging rubber material for elastic vibration isolation element and preparation method thereof

A technology of vibration isolation components and rubber materials, which is applied in the field of anti-aging rubber materials and its preparation, and can solve problems such as low dynamic-to-static ratio and poor aging resistance

Inactive Publication Date: 2008-03-19
725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
View PDF0 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to overcome the harm caused by vibration pollution to people, the object of the present invention is to provide an anti-aging rubber material for elastic vibration isolation components and its preparation method. Through the optimization of material vulcanization system, filler system

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 2

[0019] First, 80 parts of natural rubber (by weight), 20 parts of neoprene, 5 parts of zinc oxide, 2 parts of stearic acid, 1 part of antioxidant D, 1 part of antioxidant AW, 2 parts of antioxidant 4010NA, 1 part of paraffin, half-fill 40 parts of strong carbon black, 10 parts of high wear-resistant carbon black, 10 parts of white carbon black, 0.5 parts of accelerator M, 2 parts of accelerator TT, 0.5 parts of sulfur, 1 part of accelerator NA-22, 10 parts of light magnesium oxide ;The ratio of various materials is under certain process conditions, and the raw rubber is masticated on the rubber mixer, and the roller distance is controlled below 1mm. Smooth, without large particles and holes, cooling water is passed through the whole process, and the mixing can be carried out after parking for more than 4 hours after plasticizing; the order of mixing and feeding is as follows: add raw rubber after plasticizing, and add about half of it after wrapping Carbon black, white carbon ...

specific Embodiment approach 3

[0021] First, with 100 parts of natural rubber (weight ratio), 5 parts of zinc oxide, 2 parts of stearic acid, 1 part of antioxidant D, 2 parts of antioxidant AW, 2 parts of antioxidant 4010NA, 3 parts of paraffin, 30 parts of semi-reinforcing carbon black, 10 parts of high wear-resistant carbon black, 5 parts of white carbon black, 0.3 parts of accelerator TT, 1.5 parts of accelerator CZ, 2.5 parts of sulfur; the ratio of various materials is under certain process conditions, and raw rubber is plasticized on the rubber mixer. For refining, the roller distance is controlled below 1mm. After the raw rubber is covered with rolls, it is rolled into a triangular bag or rolled for refining until the surface of the film is relatively smooth without large particles or holes. Cooling water is passed through the whole process, and it is parked after plasticizing. Mixing can be carried out after more than 4 hours; the order of mixing and feeding is: add the raw rubber after mastication, ...

specific Embodiment approach 4

[0023] First, with 100 parts of natural rubber (weight ratio), 10 parts of zinc oxide, 1 part of stearic acid, 1 part of antioxidant D, 3 parts of antioxidant AW, 2 parts of antioxidant 4010NA, 2 parts of paraffin, 30 parts of semi-reinforcing carbon black, 10 parts of white carbon black, 2 parts of accelerator CZ, and 2 parts of sulfur; the ratio of various materials is under certain process conditions, and the raw rubber is masticated on the rubber mixer, and the roller distance is controlled below 1mm. Make a triangular bag or roll up and knead until the surface of the film is relatively smooth without large particles or holes. Cooling water is passed through the whole process, and it can be kneaded after being parked for more than 4 hours after kneading; the kneading and feeding sequence is: add the After plasticizing the raw rubber, add about half of the carbon black, white carbon black, anti-aging agent, and paraffin in turn after wrapping the roll; then gradually add the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An anti-ageing rubber material used for elastic vibration isolating element is formed by rubber base material, an anti-aging system, a stuffing system and a sulfurization system, wherein, the rubber base material is natural rubber or blending material mixed by natural rubber and neoprene, wherein, the weight ratio of the neoprene is 10-20 percent; the anti-aging system includes age inhibitor D, age inhibitor 4010NA, age inhibitor AW and paraffine; the stuffing system is one or more of semi-reinforcing carbon black, high wear-resistant carbon black and white carbon black; the sulfurization system includes accelerator M, accelerator TT, accelerator CZ, accelerator NA-22 and sulfur, zinc oxide, light magnesium oxide and stearic acid; the weight ratio of the material formula comprises 100 parts of rubber base, 4-10 parts of anti-aging system in total, 40-80 parts of stuffing system in total; the sulfurization system can adopt various combined proportions. The rubber material has cheap cost and good anti-aging performance, and can give the elastic vibration isolating element low dynamic to static ratio.

Description

Technical field: [0001] The invention belongs to the technical field of polymer materials, and relates to an anti-aging rubber material used for elastic vibration isolation components and a preparation method thereof. Background technique: [0002] The harm caused by vibration pollution to people has been paid more and more attention. Among them, the vibration and noise pollution of the transportation system have become one of the focuses of attention, especially in rail transportation systems such as subways and light rails. Shock waves and noise. The shock wave will propagate in the tracks, tunnels, soil layers and ground buildings, and generate corresponding vibrations, which will have a very adverse impact on the surrounding buildings and residents' lives. [0003] A commonly used solution is to apply elastic vibration isolation elements, such as track dampers, sleeper boots, ballast pads, rubber bearings, etc., to reduce the support stiffness of the track, and use the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08L11/00C08K5/09B29B7/00B29C35/02B29C43/58C08K3/04C08K3/06
Inventor 郭万涛蔡斌
Owner 725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap