Tyre crown rubber material and mixing method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of tire crown rubber and mixing, applied in special tires, tire parts, rolling resistance optimization and other directions, can solve the problems of high rolling resistance, non-conformity and poor wet skid resistance of tires, and achieve good comprehensive processing performance, low thermogenic effect
Inactive Publication Date: 2012-07-25
安徽大瑞橡胶有限公司
View PDF3 Cites 43 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Due to cost reasons, the softener oil in the formula is still commonly used ordinary aromatic oil. The finished tire made of this formula has high rolling resistance and poor wet ski
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0040] A kind of all-steel radial truck tire crown compound. The raw materials are composed of natural rubber 60~80, butadiene rubber BR9000 30, peptizer a 0~0.4, medium super wear-resistant carbon black 10~30, white Carbon black 25~45, silane coupling agent 3~7, zinc oxide 3~5, stearic acid 1~4, antioxidant 6PPD1~3, antioxidant RD 0~2, microcrystalline paraffin wax 1~3, sulfur 1~ 3. Accelerator 1.5~2.5, fatty acid salt processing aid 4~6, anti-reversion agent 0~1, environmentally friendly aromatic oil TDAE 2~5, octyl phenolic tackifying resin 1~3, anti-scorching agent 0 ~ 0.3.
Embodiment 2
[0042] A kind of all-steel radial truck tire crown compound, the weight parts of which are composed of raw materials: natural rubber 70, butadiene rubber BR9000 30, peptizer a 0.3, medium super wear-resistant carbon black N234 20, high dispersibility white carbon black 25~45, silane coupling agent 5, zinc oxide 4, stearic acid 2, antioxidant 6PPD3, antioxidant RD 1, microcrystalline paraffin 3, sulfur 2, accelerator CBS 2, fatty acid salt processing aid 5, anti-aging agent Vulcanization reversion agent PK900 1, environmentally friendly aromatic oil TDAE 3, octyl phenolic tackifying resin 3, anti-scorching agent CTP 0.1.
[0043] The specific mixing process is as follows:
[0044] 1. One stage master mixing: mixing in an internal mixer, the internal mixer speed is 35-50 rpm, the mixing steps are:
[0045] (1) Add raw rubber and peptizer into the internal mixer and mix for 20-40 seconds;
[0046] (2) Mix 1 / 2 carbon black, 1 / 2 white carbon black, silane coupling agent, and processing ai...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a tyre crown rubber material. The tyre crown rubber material comprises the following raw materials in parts by weight: 60-80 of natural rubber, 20-40 of butadiene rubber BR9000, 0-0.4 of peptizer, 10-30 of intermediate super abrasion furnace black, 25-45 of white carbon black, 3-7 of silane coupling agent, 3-5 of zinc oxide, 1-4 of stearic acid, 1-3 of antiager 6PPD, 0-2 of antiager RD, 1-3 of microcrystalline paraffin, 1-3 of sulfur, 1.5-2.5 of accelerator, 4-6 of fatty acid salt processing agent, 0-1 of anti-reversion agent, 2-5 of environment-friendly arene oil TDAE (Treated Distillate Aromatic Extract), 1-3 of octyl phenolic aldehyde tackifying resin and 0-0.3 of scorch retarder. When mixing is carried out in three sections, partial formula raw materials are subjected to rubber material mixing, and then other formula materials are added for rubber material mixing. The tyre crown rubber material produced by using the tyre crown rubber material formula is good in comprehensive processing property, has the characteristics of low thermogenesis, ageing resistance and tearing resistance and is environment-friendly and can be used for producing green full-steel radial tyre crown.
Description
technical field [0001] The invention relates to the rubber field, in particular to a tire crown rubber material and a mixing method thereof. technical background [0002] As the number of cars continues to increase, the negative impact it brings is also increasing. According to some data, more than 200 million tons of carbon monoxide are emitted into the atmosphere by automobiles every year, accounting for more than 1 / 3 of the total amount of poisonous gas, making it the largest amount of poisonous gas in the urban atmosphere. On the other hand, the contradiction between huge energy consumption and dwindling oil resources is becoming increasingly prominent. At the same time, consumers' requirements for low fuel consumption and high environmental protection are also increasing day by day. [0003] As one of the key load-bearing components of a car, tires have an important impact on the fuel economy, safety and handling of the car. The rolling resistance of tires accounts f...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).