Color coated antifouling conductive cloth and manufacturing method thereof

A manufacturing method and technology of conductive cloth, applied in the field of conductive cloth, can solve the problems of color limitation of conductive cloth, insufficient blackness to show bright, easy to be affected by the environment, etc.

Active Publication Date: 2008-03-19
FORMOSA TAFFETA CO LTD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the blackness of carbon black is not enough to show a bright blackness, and there is even only a single black option, which greatly limits the choice of product applications
[0005] There is a real need for improvement as existing conductive fabrics have drawbacks such as color limitations and susceptibility to environmental influences

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1: Preparation of antifouling conductive cloth coated with color

[0021] The following steps were carried out to obtain the color-coated antifouling conductive cloth:

[0022] Weaving fabric: Woven with polyester fiber with warp 50 denier / 36 fiber count, weft 50 denier / 72 fiber count, warp density 152 / inch and weft density 124 / inch, and thickness 0.1mm plain weave fabric.

[0023] Electroless plating: After the fabric is scoured, cleaned, heat-set, surface roughened and adjusted, electroless copper and nickel plating is carried out to metallize the fabric;

[0024] Wherein the electroless plating is a process well known to those skilled in the art, which comprises the following steps, activation: at 30°C, the cloth is mixed with palladium chloride 100mg / L, tin protochloride 10g / L and hydrochloric acid 100ml / L Immerse in the solution for 3 minutes, and then wash it completely; then speed up: at 45°C, soak the cloth in hydrochloric acid 100ml / L for 3 minutes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present relates to antifouling conducting cloth being coated with a color and the manufacturing method thereof. The method comprises the following steps: a conducting cloth provided with a metal layer and waved by natural fiber or artificial fiber is provided, and at least one colored resin coating layer is formed on the metal layer with knife coating mode, wherein, the surface of the resin coating layer is not higher than the cross salient point of the yarn in the weft and warp direction of the conducting cloth. The conducting cloth of the present invention is characterized in that the cloth has colored appearance, can prevent man induced or environmental contamination, and has low surface resistance.

Description

technical field [0001] The invention relates to the technical field of conductive cloth, in particular to a color-coated antifouling conductive cloth with low surface resistance, and a manufacturing method thereof. Background technique [0002] Existing conductive fabrics are generally electroless plated to form metallized fabrics. When copper is electroplated, the conductive fabric has a metallic copper color, copper-plated nickel-plated silver-gray, silver-plated silver-white or gold-plated gold. The conductive cloth is soft, smooth and breathable, and has the advantages of light weight and easy cutting. However, due to the metallization of the surface of the conductive fabric, the conductive fabric cannot be dyed by common fabric dyeing techniques. Compared with common fabrics with diverse colors, the conductive fabric has a monotonous appearance and has greater limitations in application. [0003] In addition, since the surface layer of the conductive cloth is made of m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D1/00D06Q1/04D06N3/00
CPCD06M11/83C23C18/1635D06N3/0063D06M2200/00D06M10/06C23C18/31D06N7/00C23C18/30C23C18/1651C23C18/48D06N7/0094D06N2209/046D06N2209/041D06N2209/0807
Inventor 张峯彰卓新峰郑建文
Owner FORMOSA TAFFETA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com