Method for preparing medicine coating carrier and medicine coating blood vessel support

A drug-coated, vascular stent technology, applied in stents, medical science, surgery, etc., can solve the problems of degradation and shedding, easy to produce inflammatory reactions, etc., and achieve the effect of not easy to fall off, less inflammation and fibrosis in the body, and good tissue response

Active Publication Date: 2008-03-26
HARBIN MEDICAL UNIVERSITY
View PDF0 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention provides a method for preparing a drug-coated carrier and a drug-coated stent in order to solve the problem that the drug-coated carrier on the existing drug-coated vascular stent is prone to inflammatory reactions and easily degrades and falls off during the degradation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing medicine coating carrier and medicine coating blood vessel support

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0014] Specific Embodiment 1: The drug-coated carrier of this embodiment is prepared according to the following method: take 0.2-1 parts of degradation regulator, 1-2.5 parts of sebacic acid and 0.8-1.2 parts of glycerin in 130-160 Prepolymerize for 6-10 hours under the condition of ℃, add 20%-50% of the total weight of sebacic acid and glycerin, and mix evenly to obtain the drug-coated carrier; the degradation regulator is glycolic acid, lactic acid, Glycolide, lactide, chitin, polyglycolic acid, polylactic acid or chitosan.

specific Embodiment approach 2

[0015] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is: 0.4-0.8 parts of degradation regulator, 1.4-2 parts of sebacic acid and 0.9-1.1 parts of glycerin are taken at 140-150° C. Pre-polymerization under certain conditions for 7 to 9 hours. Other steps and parameters are the same as those in Embodiment 1.

specific Embodiment approach 3

[0016] Embodiment 3: The difference between this embodiment and Embodiment 1 is: 0.6 parts of degradation modifier, 1.7 parts of sebacic acid and 1 part of glycerin are prepolymerized at 145°C for 8 hours in molar ratio. Other steps and parameters are the same as those in Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a preparation method of medicine coating carrier and medicine coating blood vessel scaffold. The preparation method of said medicine coating carrier includes the following steps: prepolymerization and mixing so as to obtain the medicine coating carrier, and the preparation method of said medicine coating blood vessel scaffold includes the following steps: (a), prepolymerization and mixing; and (b), polycondensation.

Description

technical field [0001] The invention relates to a preparation method of a drug coating and a drug support. Background technique [0002] The drug-coated carriers on the drug-coated stents currently developed include polylactic acid, polyglycolic acid, polypropylene oxide, and polyorthoesters. The main disadvantage of the drug-coated carrier is that additional catalysts and solvents need to be added during the synthesis process. , have a negative impact on biocompatibility, and are prone to inflammatory reactions, and the drug coating carrier is coated on the stent after synthesis, and the binding force with the stent is not strong. During the degradation and release of the drug, the drug coating is prone to large Area detachment, especially as a coronary stent, brings danger to the life of the patient. Contents of the invention [0003] In order to solve the problem that the drug-coated carrier on the existing drug-coated vascular stent is prone to inflammatory reaction a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L31/16A61L31/06A61F2/82
Inventor 董德利孙志洁鲁玺丽杨宝峰
Owner HARBIN MEDICAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com