Fluorapatite alkyd rust-inhibiting paint

A technology of calcium phosphate alkyd and calcium fluoride phosphate, which is applied in the field of paint making, can solve the problems of increasing the cost of coating and the ineffective use of resources, and achieves the effect of strong corrosion inhibition

Inactive Publication Date: 2008-05-21
武汉市大汉科技发展有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This increases the cost of coating, so

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Calcium fluorophosphate alkyd antirust paint component weight of the present invention is Kg:

[0033] Alkyd resin 38

[0034] Calcium Fluorophosphate Antirust Powder 55

[0035] Dispersant 923S 1

[0036] Organic bentonite 5

[0037] Composite dry material catalyst 1

[0038] Xylene 1

[0039] 1. First, add 15Kg of alkyd resin to the dispersant 923S1Kg. After pre-mixing for 5-10 minutes, disperse and evenly add 5Kg of organic bentonite and mix evenly, then add 1Kg of xylene solution and mix evenly, and finally add 1Kg of compound dry The catalyst is mixed evenly.

[0040] 2. Disperse and add 55Kg of calcium fluorophosphate anti-rust powder to fully stir and grind until the fineness specified by the state is reached, then add the remaining 23Kg of alkyd resin and stir evenly, then filter, inspect, subpackage, and store.

Embodiment 2

[0042] Calcium fluorophosphate alkyd antirust paint component weight of the present invention is Kg:

[0043] Alkyd 45

[0044] Calcium Fluorophosphate Antirust Powder 35

[0045] Dispersant YB201A 2

[0046] Anti-settling agent 201P 9

[0047] Composite dry material catalyst 1

[0048] 200# 8

[0049] 1. First, add 18Kg of alkyd resin to 2Kg of YB201A dispersant and pre-mix for 5-10 minutes, then disperse and evenly add 9Kg of anti-sedimentation agent 201P and mix evenly, then add 8Kg of 200# solution and mix evenly, and finally add 1Kg to compound The dry material catalyst is mixed evenly.

[0050] 2. Disperse and add 35Kg of calcium fluorophosphate anti-rust powder and fully stir and grind until the fineness specified by the state is reached, then add the remaining 27Kg of alkyd resin and stir evenly, then filter, inspect, sub-package, and store.

Embodiment 3

[0052] Calcium fluorophosphate alkyd antirust paint component weight of the present invention is Kg:

[0053] Alkyd 48

[0054] Calcium Fluorophosphate Antirust Powder 45

[0055] 923S, YB201A mixture 1

[0056] Organic bentonite 3

[0057] Composite dry material catalyst 0.8

[0058] Xylene, 200# mixture 2.2

[0059] 1. First, add 15Kg of alkyd resin to 1Kg of 923S and YB201A dispersant. After pre-mixing for 5-10 minutes, disperse and evenly add 3Kg of anti-sedimentation agent organic bentonite and mix evenly, then mix xylene and 200# mixture Add 2.2Kg of the agent and mix evenly, and finally add 0.8Kg of composite dry material catalyst and mix evenly.

[0060] 2. Disperse and add 45Kg of calcium fluorophosphate anti-rust powder to fully stir and grind until the fineness specified by the state is reached, then add the remaining 33Kg of alkyd resin and stir evenly, then filter, inspect, subpackage, and store.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an antirust paint of calcium fluophosphate alkyd. The composition has the following weight percentages: 38 weight percent to 58 weight percent of alkyd resin, 35 weight percent to 55 weight percent of rust-proof powder of calcium fluophosphate, 1 weight percent to 3 weight percent of dispersing agent, 1 weight percent to 10 weight percent of anti-settling agent, 1 weight percent to 2 weight percent of dried material and 1 weight percent to 8 weight percent of mixed solvent. The invention has the following advantages: the antirust powder of white composite silicon and titanium of excellent performance and reasonable price is used for replacing lead red and has no poisonous damage to people and the biological environment; other colors, fillers and auxiliary agents are skillfully used for getting the unique white color. At the same time, the paint has strong steel compatibility and strong corrosion-delaying performance of anode; the salt-resistant dipping time can reach above 600 hours (the national standard salt-resistant dipping time of alkyd and epoxy lead red is 24 hours to 96 hours); the neutrality-resistant and salt fog resistant time is more than 200 hours; the coating quantity in unit area is only 30 percent to 40 percent of the lead red.

Description

technical field [0001] The invention relates to the technical field of paint making, in particular to a calcium fluorophosphate alkyd antirust paint. Background technique [0002] Industry competition is becoming increasingly fierce, products are constantly updated, and environmental awareness is constantly improving. Although traditional products have their advantages, they need to gain their own benefits at the cost of damaging the environment. Such as Hongdan antirust paint, although the effect of antirust quality is relatively good in the current antirust paint, but due to the high lead content, it is easy to produce poisonous fog during construction and eradication of old Hongdan paint and welding, which is harmful to construction. Human injury is extremely serious and difficult to heal. The shoveled red lead paint or the red lead paint sprayed on the ground will seep into the ground or flow into the river to pollute the water quality, which is not good for human heal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/04C09D5/08
Inventor 金广泉
Owner 武汉市大汉科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap