Water-based woodenware matte varnish

A clear finish paint and woodware technology, which is applied to the device and coating of the surface coating liquid, which can solve the problems of poor chemical resistance, poor anti-adhesion, flammability and explosion, etc.

Inactive Publication Date: 2008-05-28
GUANGDONG SANVO CHEM IND TECH
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Currently used in home decoration, wood coatings in furniture production are basically solvent-based coatings, which contain a large amount of volatile organic compounds VOC, pollute the environment, damage the health of painters and consumers, and are flammable and explosive, and waste Petroleum resources, water-based wood coatings use water as the dispersion medium, low VOC content, low odor, no triphenyl, free TDI, no harm to the human body, no pollution to the environment, etc. The water-based wood coatings on the market now have the advantages of clear surface The paint has shortcomings such as water resistance, poor chemical resistance, low hardness, fullness, hand feeling, and poor adhesion resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] First, weigh the raw materials in proportion, 75g of self-crosslinking acrylic resin, 0.3g of polysiloxane defoamer, 0.3g of silicone leveling and slipping agent, 0.3g of polyether modified wetting agent, and 0.3g of polymer dispersant g. Silica matting agent 1.5g, under normal temperature and pressure, put into the dispersing tank successively under slow stirring and disperse at high speed for 20min until the fineness is less than 25um, then add 5g of dipropylene glycol methyl ether, 5g of dipropylene glycol butyl ether, polyurethane 1g of associative rheology additive, 4g of water, stir for 10-20min to make a finished product.

Embodiment 2

[0016] Weigh the raw materials according to the formula ratio, firstly mix 85g of self-crosslinking acrylic resin, 0.6g of polysiloxane defoamer, 0.6g of silicone leveling agent, 0.5g of polyether modified wetting agent, polymer dispersion 0.5g of silica matting agent, 3g of silica matting agent, under normal temperature and normal pressure, put them into the dispersion tank in turn for 30min and disperse at high speed under slow stirring until the fineness is less than 25um, then add 8g of dipropylene glycol methyl ether, 8g of dipropylene glycol butyl ether, Polyurethane associative rheological additive 3g, water 6g, stirred for 20min evenly, and finished product.

Embodiment 3

[0018] Weigh the raw materials according to the formula ratio, firstly, 77g of self-crosslinking acrylic resin, 0.4g of polysiloxane defoamer, 0.4g of silicone leveling and slipping agent, 0.4g of polyether modified wetting agent, polymer dispersion 0.4g of silicon dioxide matting agent, 2g of silica matting agent, under normal temperature and pressure, put them into the dispersion tank in turn under slow stirring for 25min at high speed until the fineness is less than 25um, then add 6.5g of dipropylene glycol methyl ether and dipropylene glycol butyl ether in turn 6g, 2g of polyurethane associative rheology additive, 5g of water, stir for 10-20min to make the finished product.

[0019] 1. Self-crosslinking acrylic resin:

[0020] Solids 43%

[0021] Solvent free

[0022] Viscosity 30~300Mpa

[0023] MFFT: 43°C

[0024] Pendulum hardness: 104S

[0025] PH: 7~8

[0026] 2. Polysiloxane defoamer

[0027] Non-volatile matter: 22~26%

[0028] Active matter: 20%

[0029] V...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flash pointaaaaaaaaaa
flash pointaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses matte transparent finish paint for the surface of wooden ware which is used for family decorates and furniture production. The formula and mixture ratio are that self-cross linking acrylic resin is 75-85, polysiloxane antifoaming agent is 0.3-0.6, organic silicon flatting and slipping agent is 0.3-0.6, polyether modified wetting agent is 0.3-0.5, macromolecular dispersant is 0.3-0.5, silica matting agent is 1.5-3, Dipropylene Glycol Methyl Ether is 5-8, propyleneglycol monobutyl ether is 5-8, polyurethane associated rheological additives are 1-3, and water is 4-6. The invention is characterized by 1, good chemical resistance, 2, excellent blocking resistance, 3, good sanding ability, 4, high hardness, 5, good waterproof property, 6, excellent fullness and hand feeling.

Description

technical field [0001] The invention relates to a wood surface finish paint applied to home decoration and furniture production. technical background [0002] Currently used in home decoration, wood coatings in furniture production are mainly solvent-based coatings, which contain a large amount of volatile organic compounds VOC, pollute the environment, damage the health of painters and consumers, and are flammable and explosive, and waste Petroleum resources, water-based wood coatings use water as the dispersion medium, low VOC content, low odor, no triphenyl, free TDI, no harm to human body, no pollution to the environment, etc. The water-based wood coatings on the market now have the advantages of clear surface Paint has disadvantages such as water resistance, poor chemical resistance, low hardness, fullness, hand feeling, and poor adhesion resistance. Contents of the invention [0003] The object of the present invention is to provide a kind of water-based woodware ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/00C09D7/00B05D7/06
Inventor 陈炳强陈炳辉陈明毅
Owner GUANGDONG SANVO CHEM IND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap