Method for smelting ultra-low-carbon steel

An ultra-low carbon steel, converter smelting technology, applied in the manufacture of converters and other directions, can solve the problems of plugging rod and nozzle channel blockage, etc., to reduce secondary oxidation, improve the quality of molten steel, and avoid blockage.

Inactive Publication Date: 2008-07-09
BENGANG STEEL PLATES
View PDF1 Cites 42 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The task of the present invention is to provide a method for smelting ultra-low carbon steel that solves the problems ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] This method includes: hot metal pretreatment desulfurization, slag removal→converter smelting, slag blocking, tapping without deoxidation→LF top slag modification, desulfurization→RH vacuum forced decarburization, alloying, temperature adjustment→casting machine casting.

[0013] First, desulfurize the molten iron in the molten iron pretreatment device, that is, add a desulfurizer composed of magnesium powder and lime powder to the molten iron, the weight ratio between magnesium powder and lime powder is 1:3, and use stirring, slag removal, etc. Conventional steps, when the sulfur weight content in molten iron is less than or equal to 0.004%, it is transferred to a converter for smelting;

[0014] Converter smelting: Desulfurized molten iron is smelted into molten steel by blowing oxygen to reduce carbon in the converter. The oxygen blowing time is usually between 12-18 minutes. Phosphorus and further desulfurization and other harmful elements, after sampling and testin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a process for smelting ultra-low-carbon steel, which comprises melted iron pretreatment desulfuration, converter smelt, LF furnace refining, RH vacuum process and continuous casting procedure in turn. Converter smelt tapping adopts non deoxidization tapping, steel which is tapped off is refined by LF ladle furnace before carried out melt iron vacuum decarburization processing, wherein refining is mainly used to proceed modifying property processing and further desulfuration and heating for top slag of melted iron, and the melted iron is reinforced with positive oxygen blowing decarburization after shifted into a RH vacuum container. The process can control carbon, nitrogen and sulfur in steel to preset objects which are required, and has excellent castability when a casting machine casted, thereby realizing casting by several furnaces.

Description

Technical field: [0001] The invention relates to a method for smelting ultra-low carbon steel. Background technique: [0002] Ultra-low carbon steel refers to special steel whose carbon content accounts for less than 0.01% of the total weight of the steel. The existing smelting technology can reduce the carbon content to the required level. Carbon is a simple and cheap way to increase the strength of steel. However, when the content of carbon in steel increases, some properties such as formability, weldability and toughness of steel will also weaken. With the basic and secondary effects of microalloying elements in steel, the concept of "austenite adjustment" is put forward, and the addition of microalloying elements in steel is consciously controlled to develop steel types with better performance, ultra-low Carbon steel is a steel grade that adopts microalloying technology to obtain high strength in low carbon steel and at the same time has the desired properties. [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21C7/064C21C7/068C21C5/28
Inventor 林东于华财宋满堂李明光王会忠
Owner BENGANG STEEL PLATES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap