Polyester fiber modified by hydrolysis-resisting agent and producing method thereof

A technology of polyester fiber and anti-hydrolysis agent, applied in the direction of fiber chemical characteristics, single-component polyester rayon, textile and papermaking, etc., can solve the problems of no fundamental breakthrough, high cost, etc., and achieve low cost , the effect of improving anti-aging performance and improving hydrolysis resistance

Inactive Publication Date: 2008-07-09
JUNMA TIRE CORD
View PDF0 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many studies on the modification of polyester resin by using anti-hydrolysis agents, and it has been popularized and applied in industries such as engineering plastics (films) and industrial...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] According to the proportion of 99 parts of polyester fiber raw materials (chips) and 1 part of carbodiimide monomer, they are continuously and synchronously fed into the mixing silo through the metering device for stirring and mixing. The mixture after stirring and mixing is continuously fed to the spinning screw, and The melt spinning is extruded by a screw, and the modified fiber is processed by a high-temperature and high-speed drafting roller and a winding machine.

Embodiment 2

[0014] According to the ratio of 99.5 parts of polyester fiber raw materials (chips) and 0.5 parts of carbodiimide monomer, they are continuously and synchronously fed into the mixing silo through the metering device for stirring and mixing. The mixture after stirring and mixing is continuously fed to the spinning screw, and The melt spinning is extruded by a screw, and the modified fiber is processed by a high-temperature and high-speed drawing roll and a winding machine.

Embodiment 3

[0016] According to the ratio of 99.9 parts of polyester fiber raw material (chips) and 0.1 part of carbodiimide monomer, it is continuously and synchronously sent to the mixing silo through the metering device for stirring and mixing. The mixture after stirring and mixing is continuously fed to the spinning screw, and The melt spinning is extruded by a screw, and the modified fiber is processed by a high-temperature and high-speed drafting roller and a winding machine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses polyester fiber which is modified by anti-hydrolytic reagent, which comprises anti-hydrolytic reagent carbodiimide 0.1-1% and polyester fiber 99-99.9%. The modified polyester fiber is prepared through adding anti-hydrolytic reagent carbodiimide in spinning screw bolt and mixing with high viscosity polyester welding flux to do composite spinning. The physical-mechanical properties of polyester fiber which is modified by anti-hydrolytic reagent of the invention completely achieves processing behavior of polyester fiber in common industry, ageing resistance under the environment of acid or high moisture high temperature is greatly improved, and the application field of the invention can be extended to various field of marine fishing net, tire cord yarn and the like. Difficulty of process technology of modified fiber is not complex, the line for manufacturing technique of the traditional chemical fiber need not to change, the invention is applied to commercial manufacture, cost of modified polyester fiber compared with other fiber (such as nylon) which is used at present is greatly reduced, and economic benefit is distinctive.

Description

Technical field [0001] The invention relates to a polyester fiber and a production method thereof, in particular to a polyester fiber modified with an anti-hydrolysis agent and a production method thereof. Background technique [0002] Due to its superior physical and chemical properties and lower cost, polyester fiber has become more and more widely used. However, because polyester contains ester bonds, and ester bonds are very sensitive to hydrolysis in the presence of water at higher temperatures, the hydrolysis reaction will cause the molecular chain to break at the ester bond, which will seriously affect the subsequent processing performance and limit its use. . Therefore, the research on the modification of polyester has attracted the attention of scientific and technical personnel from all over the world, and the modification of resistance to hydrolysis has become a hot spot. At present, there are many studies on the modification of polyester resins with anti-hydrolysis ag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F6/92D01F1/10
Inventor 胡永笑杨峰付洪波
Owner JUNMA TIRE CORD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap