Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cold-worked tool steel, a general-purpose technology, applied in the field of tool steel in the field of metal material technology, can solve the problem that the wear resistance needs to be improved, and achieve the effect of good comprehensive mechanical properties and good hardness
Inactive Publication Date: 2008-08-27
SHANGHAI JIAO TONG UNIV +1
View PDF2 Cites 9 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
It can be considered that this patent and the base steel 6Cr4W3Mo2VNb are high-strength and tough steels, and the wear resistance still needs to be improved
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0029] Example 1: After the steel ingot was heated at 1160°C and rolled into 100 rounds, it was slowly cooled, annealed, and finished;
Embodiment 2
[0030] Example 2: After the steel ingot was heated at 1160°C and rolled to 90 square meters, it was slowly cooled, annealed, and finished;
Embodiment 3
[0031] Example 3: The red steel ingot is heated and rolled into a 86×255 billet, heated after grinding, rolled into a 56×255 slab, slowly cooled, annealed and finished.
[0032] 3. Embodiment Cutting die blank preparation
[0033] Embodiment 1 is sawed and cut into billets;
[0034] Embodiment 2 (saw block) is hammered and upset into a circle and billeted, and the process is by the current process of A2 steel;
[0035] Example 3 Hot rolling into plates, punching / cutting and blanking, the process follows the current process of A2 steel.
[0036] 4. Embodiment Cutting die manufacturing
[0037] Cutting die blank machining - heat treatment (quenching and tempering) - finishing into cutting tools and molds
[0038] 5. Example 1: After heat treatment, the hardness is 63HRC, and the initial use is good;
[0039] Example 2: After heat treatment, the hardness is 63.7HRC, and the preliminary use condition is good;
[0040] Example 3: The hardness after heat treatment is 61.8HRC, a...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a universal cold work tool steel, which belongs to the technical field of material, wherein the components and the percentage by weight are that C 0.90-1.10, Si 0.70-1.30, Mn 0.30-1.00, P<=0.030, S<=0.030, Cr 4.00-5.50, Mo 0.50-1.00, W 1.00-1.90, V 0.75-1.20 and the allowance is Fe. Compared with cold work die steel of chrome 12 system and chrome 8 system which are extensively used, the universal cold work tool steel has better hardness, better abradability and the matching between and toughness and hot hardness and better comprehensive mechanical properties, which can be used to manufacture alloy tool steel, cutting tool and die. The invention provides a high-performance cold work tool steel, which can be selective to use.
Description
technical field [0001] The invention relates to a tool steel in the technical field of metal materials, in particular to a general-purpose cold work tool steel. Background technique [0002] Cold-work alloy tool steels are all high-carbon steels, and most of them are high-alloy steels. According to the mass percentage of the main alloying element Cr, it can be divided into three series: 12Cr, 8Cr and 5Cr. [0003] The 12Cr series is a high-Cr cold work alloy tool steel with good hardenability, high hardness and high wear resistance, and is the most widely used. The representative steel grade is Cr12Mo1V1 (D2) of the national standard GB / T1299 series of alloy tool steel. After electric machining is generally used to manufacture molds, D2 is easy to deform and crack after wire cutting due to poor toughness; D2's thermohardness-the weak resistance to softening also limits its use under high-speed and accompanied by temperature rise conditions. [0004] The 8Cr series is a med...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more