Gypsum cast material for melt mould casting
A technology of investment casting and casting mold, which is applied in casting molding equipment, casting molds, casting mold components, etc., and can solve the problem of South Korea's inability to produce gypsum casting materials.
Inactive Publication Date: 2008-10-22
SANYU CO LTD
View PDF0 Cites 11 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0006] However, since South Korea cannot produce plaster casting materials for investment casting, all materials are imported
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0021] A mold was prepared by mixing 30 wt% of 10 μm cristobalite, 50 wt% of 30 μm cristobalite (CS200, produced by Korea Semiconductor), 19 wt% of 100 μm α-gypsum, 0.5 wt% of time regulator and 0.5 wt% of paint enhancer Material.
Embodiment 2
[0023] A casting material was prepared by mixing 35 wt % 10 μm cristobalite, 45 wt % 30 μm cristobalite, 19 wt % 100 μm alpha gypsum, 0.5 wt % time modifier and 0.5 wt % paint enhancer.
Embodiment 3
[0025] A casting material was prepared by mixing 40 wt % 10 μm cristobalite, 40 wt % 30 μm cristobalite, 19 wt % 100 μm alpha gypsum, 0.5 wt % time regulator and 0.5 wt % paint enhancer.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a gypsum mould material for casting a precision fusible pattern, characterized in that the gypsum mould material is prepared by respectively mixing 30 to 50% by weight of 10 mum cristobalite, 35 to 60% by weight of 30 mum cristobalite, 15 to 25% by weight of alpha gypsum, 1 to 5% by weight of time regulator and a coating intensifier. By using noble metals such as gold, silver and platinum, the invention can be used for preparation of the precision casting. The mould procedure can be carried out even at high temperature when injecting the molten metal, no crack will be generated and excellent dispersivity is obtained.
Description
technical field [0001] The present invention relates to a plaster mold material for investment casting, and in particular a plaster mold material for investment casting in which precision castings can be produced using precious metals such as gold, silver, platinum, and the like. Even if the molding process is performed at a high temperature when injecting molten metal, no cracks are generated and good dispersion is obtained. Background technique [0002] The investment casting process is usually divided into replica casting, leadcasting and lost wax casting. Lost wax casting, or lost foam casting, is also known as investment casting. This casting process has been used by dentists and precious metal workers since the times of ancient Egypt and ancient China, and it has actually become part of the industry after World War II. In the aerospace industry, investment casting uses metals with high melting points to create precision and complex shapes that are not easy to handle,...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B22C1/00B22C3/00
CPCB22C1/04B22C1/08B22C1/18
Inventor 朴昭炫
Owner SANYU CO LTD