Nanometer type reinforced nylon 6 composition and method of preparing the same

A nano-type and composite technology, which is applied in the field of nano-type reinforced nylon 6 composition and its preparation, can solve the problems of glass fiber exposure and other problems, and achieve the effects of improving product physical properties, high rigidity, reducing weight and cost

Inactive Publication Date: 2008-12-17
PINGDINGSHAN HUABANG ENG PLASTIC
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a novel nano-type reinforced nylon 6 composition and its preparation method in view of the characteristics of the widely used nylon plastics, which not only solves the problem of glass fiber exposure in the injection molding process of engineering plastics, but also improves the quality of the product. The appearance quality has improved the physical properties of the product, especially the bending strength has more than doubled that of ordinary reinforced plastics, which has improved the product to a new level and changed the pattern of some domestic manufacturers relying on imports

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A nano-type reinforced nylon 6 composition, which is obtained by blending the following main raw materials and extruding them at 215-250°C:

[0032] Nylon 6 slices 23Kg

[0033] Glass fiber 11Kg

[0034] 168 70g

[0035] 1076 70g

[0036] EBS 350g

[0037] Powdered silica 160g

[0038] KH560 65g

[0039] The method for preparing the nanotype reinforced nylon 6 composition of the present invention, its main steps are:

[0040] In the first step, add 70g 168, 70g 1076, and 350g EBS into the mixer and mix for 1 minute, and the resulting mixture is ready for use;

[0041] The second step is to dry the nylon 6 slices at a temperature of 90°C for 6 hours;

[0042] The third step is to add 23Kg of dried nylon 6 chips, 11Kg of glass fiber, the mixture obtained in the first step, 160g of powdered silica and 65g of KH560 into the extruder, and melt and extrude at 250°C to obtain the extrudate ;

[0043] The fourth step, the extrudate is cooled by water cooling;

[0044]...

Embodiment 2

[0046] A nano-type reinforced nylon 6 composition, which is obtained by blending the following main raw materials and extruding them at 215-250°C:

[0047] Nylon slice 6 22Kg

[0048] Glass fiber 10Kg

[0049] 168 65g

[0050] 1010 65g

[0051] TAF 320g

[0052] Powdered silica 150g

[0053] KH560 70g

[0054] The method for preparing the nanotype reinforced nylon 6 composition of the present invention, its main steps are:

[0055] In the first step, add 65g168, 65g 1010, and 320g TAF into the mixer and mix for 1 minute, and the resulting mixture is set aside;

[0056] The second step is to dry the nylon 6 slices at a temperature of 100°C for 5 hours;

[0057] The third step is to add 22Kg of dried nylon 6 slices, 10Kg of glass fiber, the mixture obtained in the first step, 150g of powdered silica and 70g of KH560 into the extruder, and melt and extrude at 240°C to obtain the extrudate ;

[0058] The fourth step, the extrudate is cooled by water cooling;

[0059] The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a nano intensified-nylon-6 composite, which is prepared by blending the following major materials according to different percentages, melting and extruding the materials under the temperature of 215 DEG C to 250 DEG C: 50 percent to 70 percent of nylon slices, 25 percent to 30 percent of glass fiber, 0.05 percent to 0.1 percent of antioxidant I, 0.05 percent to 0.1 percent of antioxidant II, 1 percent to 1.5 percent of lubricant, 0.5 percent to 1 percent of nano material and 0.25 percent to 1 percent of coupling agent; the invention needs no compatilizer and tackifier, which greatly reduces the cost, solves the problem that the glass fiber of the engineering plastics is exposed during the injection molding process, improves the appearance quality of the products and enhances the physical indexes of the products to a certain degree, thus changing the situation that some domestic manufacturers depend on the imported nylon. The composite of the invention can be used in automobile and electromechanical industry field, can be acted as thin walled complicated structural product due to the high rigidness, and is an environment protective product that can substitute the present halogenous fire retardants, which is energy conservative and environment protective and is an ideal product for the current engineering plastics modification industry.

Description

Technical field: [0001] The invention relates to the field of engineering plastics, in particular to a nanoscale reinforced nylon 6 composition and a preparation method thereof. Background technique [0002] The peripheral parts of automobile engines are mainly heat-generating and vibrating parts, so the materials used must have high comprehensive performance. However, due to the poor dispersion and fluidity of glass fibers, there are obvious weld marks and flow marks on the surface of injection molded products, and there are even glass fibers. The phenomenon of fiber exposure seriously affects the appearance of the product. Nylon has the advantages of high strength, wear resistance, solvent resistance, good self-lubricating property and wide temperature range. It has outstanding chemical resistance and oil resistance. It is the most widely used variety among the five major engineering plastics. It is now widely used in various electronic and electrical equipment. and home ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08K13/04C08K7/14C08K3/36C08J5/04B29B9/14B29C47/92B29C48/92
CPCB29C48/04B29C48/92B29C2948/92704B29C2948/92895
Inventor 刘成
Owner PINGDINGSHAN HUABANG ENG PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products