Preparation process of petroleum resin mixed by aliphatic resin and aromatic resin

A preparation process, aliphatic hydrocarbon technology, applied in building components, building insulation materials, construction and other directions, can solve the problems of shortening mixing time, high price, heavy burden, etc., to shorten mixing time, reduce wear, tear The effect of increasing crack strength

Inactive Publication Date: 2009-02-04
逯大成
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Homogenizer 40MSF has obvious effects on shortening mixing time, reducing mixing energy consumption, improving carbon black dispersion effect, and improving rubber mixing uniformity, but its

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of petroleum resin mixed by aliphatic resin and aromatic resin
  • Preparation process of petroleum resin mixed by aliphatic resin and aromatic resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Add 10g of C5 resin and 60g of C9 resin in sequence to a 500ml flask, control the reaction temperature at 180°C for 2 hours, add 30g of rubber asphalt at 180°C, and discharge after 2 hours of uniform stirring to obtain petroleum resin 40MSH product. The softening point is 95°C, the ash content is 0.4%, and the appearance is dark brown solid.

Embodiment 2

[0025] Add 8g of C5 resin and 62g of C9 resin in a 500ml flask in turn, control the reaction temperature at 190°C for 2 hours, add 31g of rubber asphalt at 190°C, and discharge after 2 hours of uniform stirring to obtain petroleum resin 40MSH product. The softening point is 97°C, the ash content is 0.5%, and the appearance is dark brown solid.

Embodiment 3

[0027] Add 9g of C5 resin and 61g of C9 resin in a 500ml flask in sequence, control the reaction temperature at 200°C for 3 hours, add 32g of rubber asphalt at 200°C, and discharge after 3 hours of uniform stirring to obtain petroleum resin 40MSH product. The softening point is 96°C, the ash content is 0.5%, and the appearance is dark brown solid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Softening pointaaaaaaaaaa
Softening pointaaaaaaaaaa
Softening pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of petroleum resin through mixing aliphatic hydrocarbon resins and aromatic hydrocarbon resins, belonging to the technical field of organic synthesis. The invention adopts C-5 resin and C-9 resin as the raw materials. The invention is characterized in that the preparation process is carried out according to the following steps: (1) C-5 resin and C-9 resin are adopted as the raw materials, which are reacted in a normal pressure reactor for more than or equal to two hours to produce fatty resins-mixture compounded by aromatic hydrocarbon resins, wherein, the reaction temperature is controlled at 180 to 200 DEG C; (2) rubber asphalt is added in the system for more than or equal to two hours to produce the finished products, wherein, the reaction temperature is controlled at 180 to 200 DEG C. The petroleum resin prepared with the method of the invention is capable of improving the mixing uniformity of rubbers of different polarity and viscosity, reducing the mixing time, improving the mobility of the rubber materials, improving the stretching strength and the physical and mechanical properties of the rubber materials, and fundamentally overcoming the influence of processing various additives on the stretching strength; the tear strength is increased and the wear loss is reduced. The product is of low price and is suitable for promotion.

Description

technical field [0001] The invention belongs to the technical field of organic synthesis, and in particular relates to a preparation technology of petroleum resin. Background technique [0002] In the tire industry, leveling agents are generally used for mixing rubbers of different polarities and viscosities. In the prior art, a leveling agent 40MSF is commonly used in tire tread rubber. Homogenizer 40MSF is an imported raw material, and currently there is no domestic enterprise that can produce it. Homogenizer 40MSF has obvious effects on shortening mixing time, reducing mixing energy consumption, improving carbon black dispersion effect, and improving rubber mixing uniformity, but its disadvantage is that it is expensive. With the rise of raw material prices, the high price of leveling agent 40MSF is obviously too much burden on domestic small and medium-sized enterprises. Contents of the invention [0003] The object of the present invention is to provide a preparati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L57/02C08L95/00C08L21/00
Inventor 逯大成梅明
Owner 逯大成
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com