Pigment dispersion and recording ink, and ink cartridge, ink jet recording method, and ink jet recording device
A technology of pigment dispersion and pigment dispersant, which is applied in the field of ink cartridges and inkjet recording devices, and can solve the problems of low printing quality, feathering, water resistance and insufficient fixing ability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation Embodiment A-1
[0377] Preparation of Solution A-1 of Polymer Dispersion Stabilizer
[0378] A mixture of the ingredients shown below was mixed with a mechanical stirrer under heating to dissolve the α-olefin / maleic anhydride copolymer (I), and then a trace amount of insoluble matter was filtered out with a filter having an average pore size of 5 μm, thereby preparing a polymer dispersion stabilizer of solution A-1.
[0379] α-Olefin / maleic anhydride copolymer (I) *1) 10.0 copies
[0380] 1N KOH aqueous solution *2) 68.62 copies
[0381] 21.38 parts of deionized water
[0382] 1) T-YP110, manufactured by Seico PMC Co., number of carbon atoms in the olefin chain: 12 to 14, acid value: 385 mgKOH / g, mass average molecular weight: 9000
[0383] 2) 1.0 times the amount of alkali, in terms of acid value
preparation Embodiment A-2
[0385] Preparation of Solution B of Polymer Dispersion Stabilizer
[0386]A mixture of the ingredients shown below was mixed with a mechanical stirrer under heating to dissolve the α-olefin / maleic anhydride copolymer (II), and then a trace amount of insoluble matter was filtered out with a filter having an average pore size of 5 μm, thereby preparing a polymer dispersion stabilizer solution B.
[0387] α-Olefin / maleic anhydride copolymer (II) *1) 10.0 copies
[0388] 1N NaOH aqueous solution *2) 28.08 copies
[0389] 61.92 parts of deionized water
[0390] 1) T-YP110, manufactured by Seico PMC Co., carbon number of olefin chain: 16 to 18, acid value: 221 mgKOH / g, mass average molecular weight: 11000
[0391] 2) 1.0 times the amount of alkali, in terms of acid value
preparation Embodiment A-3
[0393] Preparation of Solution C of Polymer Dispersion Stabilizer
[0394] A mixture of the ingredients shown below was mixed with a mechanical stirrer under heating to dissolve the α-olefin / maleic anhydride copolymer (III), and then a trace amount of insoluble matter was filtered out with a filter having an average pore size of 5 μm, thereby preparing a polymer dispersion stabilizer solution C.
[0395] α-Olefin / maleic anhydride copolymer (III) *1) 10.0 copies
[0396] 1N LiOH aqueous solution *2) 17.34 copies
[0397] 72.66 parts of deionized water
[0398] 1) T-YP112, manufactured by Seico PMC Co., number of carbon atoms in the olefin chain: 20 to 24, acid value 190 mgKOH / g, mass average molecular weight: 10000
[0399] 2) 1.2 times the amount of alkali, in terms of acid value
PUM
Property | Measurement | Unit |
---|---|---|
Acid value | aaaaa | aaaaa |
Acid value | aaaaa | aaaaa |
Acid value | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com