Dry mix sub-light powder paint

A technology of dry-mixing matte powder and matte powder, which is applied in powder coatings, polyester coatings, coatings, etc., can solve the problems of reducing powder quality and achieve the effects of good impact resistance, cost reduction, and less impurities

Inactive Publication Date: 2009-02-18
ANHUI MEIJIA NEW MATERIAL
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The matting of the traditional matt powder coating is to add matting curing agent during the powder production process, so that the powder can achieve matting effect during the curing process. The addition of this matting curing agent makes the low-temperature kneading process exist in the powder production process. As a result, impurities are formed before the powder solidifies, thus reducing the powder quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Dry mixed matt powder unpainted, composed of component A and component B,

[0036] Described component A comprises following material and parts by weight:

[0037] Polyester resin A 25

[0038] TGIC 2

[0039] BaSO 4 5

[0040] CaCO 3 2

[0041] TiO 2 1.5

[0042] Tillandsia Appropriate amount

[0043] Described component B comprises following material and parts by weight:

[0044] Polyester resin B 25

[0045] TGIC 2

[0046] BaSO 4 4.5

[0047] CaCO 3 2.5

[0048] TiO 2 0.8

[0049] High black Appropriate amount.

[0050] The acid value range of the polyester resin is 35-45MGKOH / G, the softening point range is 100-120 degrees, and the glass transition temperature (TG) is greater than 60 degrees.

[0051] Polyester resin A is formed by condensation of polybasic acid and polyhydric alcohol, produced by Anhui Shenjian Chemical Co., Ltd.

[0052] The polyester resin...

Embodiment 2

[0054] Dry mixed matt powder unpainted, composed of component A and component B,

[0055] Described component A comprises following material and parts by weight:

[0056] Polyester resin A 28

[0057] TGIC 5

[0058] BaSO 4 7

[0059] CaCO 3 5

[0060] TiO 2 2.5

[0061] Tillandsia Appropriate amount

[0062] Described component B comprises following material and parts by weight:

[0063] Polyester resin B 28

[0064] TGIC 5

[0065] BaSO 4 6.5

[0066] CaCO 3 4

[0067] TiO 2 1

[0068] High black Appropriate amount.

[0069] After mixing the coating prepared in Example 1, apply it on the substrate, the coating appearance: smooth and smooth; film thickness: 70 μm; gloss: equal to 12; impact test: equal to 50kg / cm; bending test: 1mm, adhesion: Grade 0; hardness: 2H; gel time (180 degrees) seconds: 1-3, 1'39"; particle size: pass 160 mesh: equal to 100μm, greater than or equal to 9...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
lusteraaaaaaaaaa
Login to view more

Abstract

The invention discloses dry mixed matt powder paint, which comprises component A and component B. The component A comprises the following materials by weight portion: 25 to 28 portions of vibrin A; 2 to 5 portions of TGIC; 5 to 7 portions of BaSO4; 2 to 5 portions of CaCO3; and 1.5 to 2.5 portions of TiO2. The component B comprises the following materials by weight portion: 25 to 28 portions of vibrin B; 2 to 5 portions of TGIC; 4.5 to 6.5 portions of BaSO4; 2.5 to 4 portions of CaCO3; and 0.8 to 1.0 portion of TiO2. By comparing the invention with the prior art, the dry mixed matt powder paint contains little impurity, and has excellent scratch resistance and impact resistance as well as comfortable luster, which is solventless thermoset high strength decorative antifriction material and can eliminate light when the powder is cured.

Description

technical field [0001] The invention belongs to matte powder non-coating, in particular to dry-mixed matt powder non-coating. Background technique [0002] The matting of the traditional matt powder coating is to add matting curing agent during the powder production process, so that the powder can achieve matting effect during the curing process. The addition of this matting curing agent makes the low-temperature kneading process exist in the powder production process. As a result, impurities are formed before the powder solidifies, thus reducing the powder quality. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a dry mixed matt powder coating with less impurities. [0004] The technical solution of the present invention to solve the technical problem is: dry mixed matt powder without coating, composed of component A and component B, [0005] Described component A comprises following material and parts by weig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/02C09D167/06C09D5/03
Inventor 王方银
Owner ANHUI MEIJIA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap