A gas-assisted injection molding and polyamide technology, which is applied in the field of engineering plastics, can solve problems such as weld lines and flow marks, low melt strength, and glass fiber exposure, and achieve high impact performance, good dimensional stability, and high melt intensity effect

Inactive Publication Date: 2009-05-27
SHANGHAI SUNNY
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor fluidity of ordinary glass fiber modified polyamide 6, there are obvious weld marks and flow marks on the surface of injection molded products, and even the phenomenon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Example 1-2

[0016] Using PA6 slices with a viscosity of 2.8, alkali-free glass fibers for glass fibers, kaolin for inorganic minerals, and polyolefin elastomer grafted with maleic anhydride graft polymer CMG9805 as the compatibilizer of Example 1, the compatibility of Example 2 As the agent, EPDM rubber is grafted with maleic anhydride graft polymer CMG9802, the antioxidant is 1098 / 168 (1:1), and the coupling agent is KH550.

[0017] Ratio 1-2

[0018] raw material name Mixing ratio 1 (wt%) Mixing ratio 2 (wt%) PA6 slice 54 54 glass fiber 20 20 High territory 20 20 CMG9801 5 -- CMG9802 -- 5 1098 / 168(1∶1) 0.5 0.5 KH550 0.5 0.5

[0019] According to the conventional method, put the above-mentioned raw materials except glass fiber in a high-mixer and mix for 2-5 minutes, and then use a screw extruder together with the glass fiber to extrude and granulate. The processing temperature is 200-240℃, and the screw r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a polyamide 6 composition used for gas aided injection molding, which is characterized by comprising the following compositions by weight percentage: 40 to 80 percent of polyamide 6 slice, 5 to 30 percent of fiber glass, 5 to 30 percent of inorganic mineral, 1 to 10 percent of compatilizer, 0.1 to 0.5 percent of antioxidant, and 0.1 to 0.5 percent of coupling agent. The polyamide 6 composition has the characteristics of higher melt strength, excellent dimension stability, good chemical resistance, smooth product surface and the like, and can be both used for gas aided injection molding of an automobile door pull and other automobiles and mechanical and electrical products suitable for gas aided injection molding.

Description

technical field [0001] The invention relates to a polyamide 6 composition which can be used for gas-assisted injection molding, which has the characteristics of high melt strength, excellent chemical resistance, good dimensional stability, and smooth surface of the product, and can be used for gas-assisted injection molding automobile doors The handle can also be used to process other auto parts and electromechanical products suitable for gas-assisted injection molding, and belongs to the technical field of engineering plastics. technical background [0002] Polyamide 6 has good physical and mechanical properties, such as high tensile strength, excellent wear resistance, good impact resistance, outstanding chemical resistance and oil resistance, and is the most widely used variety among the five major engineering plastics. Since car door handles and other automotive or electromechanical products are all appearance parts, the requirements for the surface finish of the product...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/02C08K9/06C08K7/14C08K5/524C08L51/06
Inventor 柴振东陈晓东
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap