Suspended reduction process for iron-containing materials and device therefor

A process method and material technology, applied in the field of iron-containing material reduction devices and iron-containing material reduction devices, can solve the problems of low production efficiency, low metallization rate, and high cost, and achieve high production capacity, large mass transfer coefficient, small footprint effect

Inactive Publication Date: 2009-06-03
LAIWU IRON & STEEL GRP
View PDF13 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the limitation of the combination of the invented equipment and process, the above disclosed patents have problems such as low metallization rate, high energy consumption, low production efficiency and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Suspended reduction process for iron-containing materials and device therefor
  • Suspended reduction process for iron-containing materials and device therefor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Iron-containing materials: iron ore fine powder; reducing gas: generating gas.

[0040] The process flow of the iron-containing material suspension reduction system is as follows: figure 1 shown. Iron-containing materials and fine powder materials with a lime particle size range of 1-40 μm are sent from the lifting device 1 to the I-stage heat exchange tube 2, and after fully exchanging heat with the high-temperature reducing gas from the II-stage cyclone preheater 5, they flow into the I Stage I cyclone preheater 3; in the stage I cyclone preheater, the suspended iron-containing material particles are separated from the reducing gas and then enter the stage II heat exchange tube 4, the reducing gas passes through the fan 13, the dust collector 14, and the reducing gas is waste Collected by the collection system 15, the outlet temperature of the waste reducing gas is 200-400°C; the preheated iron-containing material enters the II-stage heat exchange tube 4, and the iro...

Embodiment 2

[0042] Iron-containing materials: 80% iron ore fine powder, 20% iron-containing metallurgical dust; reducing gas: coke oven gas.

[0043] Such as figure 2 As shown, the coke oven gas enters the gas tank 19 after being preheated by the preheater 22 . The coke oven gas from the coke oven gas preheater 22 replaces the generated gas from the gas generator 21 . The cross section of the heat exchange tubes of the cyclone preheater is circular. Others are with embodiment 1.

Embodiment 3

[0045] Iron-containing material: 10%-90% of iron ore micropowder, 90%-10% of iron-containing metallurgical dust; reducing gas: natural gas, which replaces the coke oven gas in embodiment 2 with natural gas, and the others are the same as in embodiment 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of iron and steel metallurgy and the field of gas-solid heat exchange or thermal reaction, and relates to a device for reducing iron-containing materials, in particular to a suspended reduction process for iron-containing materials and an iron-containing material reducing device for implementing the process of quick heating, quick reaction and separation of powdery iron-containing materials. In the injection reducing furnace, the gas phase and the solid phase flow upwards in parallel and the gas phase and the solid phase are in full contact, with large heat-transfer coefficient and large mass-transfer coefficient, so that the iron-containing materials are reduced and dried quickly, and the retention time of material granules in the system is greatly shortened. The suspended reduction process has the advantages of high thermal efficiency of the system, low heat loss, good system stability, compact equipment installation, small size, low investment, high production capacity, high product metallization rate, controllable metallization rate within the range from 85% to 97%, and uniform product quality.

Description

technical field [0001] The invention belongs to the technical field of iron and steel metallurgy and the field of gas-solid phase heat exchange or thermal reaction, and relates to a reduction device for iron-containing materials, in particular to a reduction device for fast heating, rapid reduction and separation of powdery iron-containing materials . Background technique [0002] Since M.Voel-Jorgensen, a Czech engineer, first submitted the patent for heating cement raw meal powder in a cyclone suspension preheater in 1932, the quality and output of cement kilns have been greatly improved, and the heat consumption has been significantly reduced, which has attracted cement technology researchers from all over the world. and device manufacturers' concerns. In the early 1990s, the FIOR company in Venezuela and the VAI Engineering Technology Co., Ltd. in Austria jointly developed the FINMET process. This process uses iron ore powder as raw material and natural gas as the reduc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C21B13/14
Inventor 董杰李丰功王学斌曾晖王博
Owner LAIWU IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap