Method for manufacturing Chinese hemp multi-component covering type two-sided knit fabric
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for knitted fabrics and manufacturing methods, applied in knitting, weft knitting, warp knitting, etc., can solve the problems of rare clothing fabrics, achieve bright colors, enhance feasibility, and improve the effect of itching
Active Publication Date: 2009-08-05
北京铜牛集团有限公司
View PDF2 Cites 27 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
But so far, there are not many clothing fabrics that are really used in weft knitting.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0048] A method for manufacturing a hemp multi-component covered double-sided knitted fabric, comprising the steps of:
[0049] 1) Weaving
[0050]Weaving 30% hemp, 35% polyester and 35% cotton by weight into a hemp blended yarn with a yarn count of 40s, and then weaving it with moisture-absorbing and quick-drying polyester yarn on a fine-gauge knitting device to form a fabric; The weight ratio of the hemp blended yarn to the moisture-absorbing and quick-drying polyester yarn is 65:35;
[0051] 2) Pretreatment
[0052] Under the condition that the bath ratio is 1:12, the temperature of the bleaching solution is raised to 98°C at a rate of 2°C / min, the bottom is rinsed at this temperature for 30 minutes, and then the temperature is lowered to 25°C at a rate of 2°C / min and washed with water for 20 minutes ;
[0053] In the described bleaching solution, the percentage of auxiliary agent relative to fabric weight is:
[0054] h 2 o 2 4%, base substitute 3%, lubricant 1%,...
Embodiment 2
[0064] A method for manufacturing a hemp multi-component covered double-sided knitted fabric, comprising the steps of:
[0065] 1) Weaving
[0066] Weaving 30% hemp, 35% polyester and 35% cotton by weight into a hemp blended yarn with a yarn count of 40s, and then weaving it with moisture-absorbing and quick-drying polyester yarn on a fine-gauge knitting device to form a fabric; The weight ratio of the hemp blended yarn to the moisture-absorbing and quick-drying polyester yarn is 60:40;
[0067] 2) Pretreatment
[0068] Under the condition that the bath ratio is 1:12, the temperature of the bleaching solution is raised to 98°C at a rate of 2°C / min, the bottom is rinsed at this temperature for 30 minutes, and then the temperature is lowered to 25°C at a rate of 2°C / min and washed with water for 20 minutes ;
[0069] In the described bleaching solution, the percentage of auxiliary agent relative to fabric weight is:
[0070] h 2 o 2 4%, base substitute 3%, lubricant 1%,...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a manufacture method of a hemp, polycomponent, covering and double-knitted fabric, which comprises the following steps: (1), weaving 30 percent of hemp, 35 percent of terylene and 35 percent of cotton by weight percentages into hemp blended yarn with a yarn number of 40 and then weaving the hemp blended yarn with moisture-bsorbing and rapidly-drying terylene yarn into a fabric under the condition that the weight ratio of the hemp blended yarn to the moisture-bsorbing and rapidly-drying terylene yarn is 55-65 to 35-45; (2) bleaching and heating a solution at a speed of 2 DEG C/min to a temperature of 98 DEG C under the condition that a bath ratio is 1 to 12, bleaching the solution at the temperature for 30 minutes, cooling the solution at a speed of 2 DEG C/min to 25 DEG C and washing the solution for 20 minutes; (3) dyeing; and (4) post-treatment technology. The invention has the advantages that hemp fibers have wide prospects after being applied to fabrics because the hemp has natural superior characteristics of antibacterium, ultraviolet ray resistance, moisture absorbable and breathable properties, and the like, the fabric adopts the blended yarn of the hemp, the cotton and the terylene to weaken the rigidity of the blended yarn, and the hemp fabric solves the problem of scratchiness and has bright colors and high color fastness.
Description
technical field [0001] The invention relates to a method for manufacturing a textile fabric, in particular to a method for manufacturing a hemp multi-component covered double-sided knitted fabric. Background technique [0002] When people mention "hemp fiber", they will naturally think of daily necessities such as "hemp rope" and "sack", giving people the feeling that: the appearance is relatively rough and stiff, the color is dull, wear-resistant and durable, and the skin contact is not good. Comfort etc. With the development of science and technology today, with the substantial improvement of people's material living standards, the new concept of "green, environmental protection, and health" clothing has become more popular. The application of "hemp fiber" in the textile field is no longer so simple, and the content is more substantial and more Extensive, related products are becoming more and more abundant. Merchants have launched linen products such as woven casual wea...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more