Toughening modified polylactic acid composite material and method for producing the same
A composite material and a technology of toughening and modification are applied in the field of toughening and modified polylactic acid composite materials and their preparation, and can solve the problems of poor flexibility and impact resistance, limiting the large-scale popularization and application of polylactic acid, and high rigidity of polylactic acid. Achieve the effects of excellent impact resistance, excellent elongation at break, and simple preparation process
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0031] Example 1:
[0032] The weight ratio of polylactic acid is 97.9% (the following are weight ratios), TPU Elastollan C85A 1%, 1010 / 1680.2 / 0.3%, PETS 0.1%, and other additives 0.5%. The mixed materials are added to the hopper of the twin-screw extruder, melt blended, extruded and granulated into composite materials. Among them, the temperature settings of each heating zone of the screw are respectively: a zone temperature of 170°C, a zone temperature of 180°C, a zone temperature of 190°C, a zone temperature of 190°C, and a head temperature of 185°C; residence time 2 to 3 minutes, pressure It is 13Mpa.
Example Embodiment
[0033] Example 2:
[0034] The weight ratio of polylactic acid is 93.9% (the following are weight ratios), TPU Elastollan C85A 5%, 1010 / 1680.2 / 0.2%, PETS 0.1%, and other additives 0.6%. The mixed materials are added to the hopper of the twin-screw extruder, melted and blended, extruded and granulated into composite materials. Among them, the temperature settings of each heating zone of the screw are respectively: a zone temperature of 170°C, a second zone temperature of 180°C, a third zone temperature of 190°C, a fourth zone temperature of 190°C, and a head temperature of 185°C; residence time 2 to 3 minutes, pressure It is 13Mpa.
Example Embodiment
[0035] Example 3:
[0036] The weight ratio of polylactic acid is 88.9% (the following are weight ratios), TPU Elastollan C85A 10%, 1010 / 1680.3 / 0.2%, PETS 0.1%, and other additives 0.5%. The mixed materials are added to the hopper of the twin-screw extruder, melt blended, extruded and granulated into composite materials. Among them, the temperature settings of each heating zone of the screw are respectively: a zone temperature of 170°C, a second zone temperature of 180°C, a third zone temperature of 190°C, a fourth zone temperature of 190°C, and a head temperature of 185°C; residence time 2 to 3 minutes, pressure It is 13Mpa.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap