Fe-based amorphous alloy material and method of producing the same

An alloy material, iron-based amorphous technology, applied in the field of amorphous alloy soft magnetic materials, can solve the problems of difficult to guarantee the quality of the strip, high strip-making process conditions, and high requirements for the smelting process, and achieve comprehensive magnetic properties and mechanical properties. Good performance, good processability, and wide application range

Inactive Publication Date: 2010-06-30
北京晶鑫联合新材料科技有限公司
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problem with the amorphous alloy strip is that the strip-making process conditions are high, the strip surface made of strip has many sand holes, and the quality of the strip is difficult to be guaranteed.
The main problem of the amorphous alloy material is that the carbon content is high, the smelting process requires high requirements, the process is complicated, and the carbon content in smelting is unstable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1) Prepare raw materials such as pure iron, pure silicon, ferroboron, chromium, copper and cast iron powder. The weight ratio of chemical components in the raw materials is as follows: iron 92kg, silicon 6kg, boron 3kg, chromium 0.2kg, copper 0.02kg, carbon 0.1 kg.

[0033] Among them, boron comes from ferroboron with a boron content of 17%, and carbon comes from cast iron powder with a carbon content of 30%, so iron is the sum of the weight of industrial pure iron, ferroboron and iron in cast iron powder.

[0034] 2) Loading, vacuuming, heating

[0035]Put all the pure iron into the vacuum smelting furnace (produced by Xiangtan Electric Furnace Factory; power 100KW), and then sequentially load chromium, silicon, ferroboron, copper and cast iron powder raw materials, cover the vacuum smelting furnace tightly, and start the machine The pump evacuates the vacuum furnace. When the relative vacuum of the vacuum smelting furnace reaches 200Pa (that is, the vacuum pressure i...

Embodiment 2

[0048] Prepare raw material pure iron, pure silicon, boron iron, chromium, copper and cast iron powder, make in the raw material have the chemical composition of following weight ratio: iron 93kg, silicon 6.05kg, boron 2.5kg, chromium 0.15kg, copper 0.02kg, Carbon 0.09kg.

[0049] Other than that, it is the same as in Example 1. The product technical performance index detection of the obtained iron-based amorphous alloy strip is shown in Table 1.

Embodiment 3

[0051] Prepare raw material pure iron, pure silicon, ferroboron, chromium, copper and cast iron powder, make in the raw material have the chemical composition of following weight ratio: iron 91.0kg, silicon 6.15kg, boron 2.90kg, chromium 0.18kg, copper 0.018kg , carbon 0.12kg.

[0052] Other than that, it is the same as in Example 1. The product technical performance index detection of the obtained iron-based amorphous alloy strip is shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an amorphous alloy material with Fe as the main component and a preparation method thereof. The amorphous alloy material of the invention comprises the chemical components with the following parts by weight: Fe: 91.0-93.5; Si: 5.2-6.6; B: 2.5-3.3; Cr: 0.05-0.25; Cu: 0.010-0.030; and C: 0.05-0.20. The Fe-based amorphous alloy belt material has simple design in components, and good mechanical property and fine processability of the material; moreover, yield is over 90%. In addition, the manufactured Fe-based amorphous alloy belt material has high comprehensive magnetic property; and coreloss of a transformer manufactured by the amorphous alloy material is greatly reduced. The Fe-based amorphous alloy belt material enjoys wide application and low use cost and serves tosave energy and protect the environment.

Description

technical field [0001] The invention relates to an amorphous alloy soft magnetic material, in particular to an amorphous alloy soft magnetic material with iron as the main component. Background technique [0002] Amorphous material is a new type of "superconducting magnetic" material born in the 1970s. Amorphous material and its preparation process are internationally recognized as a revolutionary progress in metal materials and metallurgical processes. Known as green material. The main raw materials of these amorphous materials are iron, silicon, boron, etc. Usually, the quenching technology of quenching and solidifying the master alloy from the molten state is used to prepare amorphous alloy thin strips, which are cast into thin strips by rapidly solidifying them. The thickness of the ribbon is less than a quarter of that of a human hair, and finally an amorphous alloy ribbon with short-range order and long-range disorder in the arrangement of atoms is obtained. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C45/02C22C1/03
Inventor 吴更生吴海
Owner 北京晶鑫联合新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap