Safe infusion apparatus and preparation method thereof

An infusion set, safe technology, applied in the field of safety infusion sets and preparations, can solve the problems of infusion set damage, pipeline entanglement, leakage, etc., and achieve excellent mechanical properties, good bonding performance, and good compatibility Effect

Active Publication Date: 2011-08-10
SHANDONG WEIGAO GROUP MEDICAL POLYMER +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] (1) The surface of the non-PVC infusion set is sticky, and the pipeline will be entangled during storage or use.
[0008] (2) The mechanical properties of non-polyvinyl chloride infusion materials are poor, and the prepared infusion set tubes are easily deformed or broken under stress
[0009] (3) The non-polyvinyl chloride infusion material has poor bonding performance, and the infusion set will be damaged and leak during use.
[0010] (4) The cost of raw materials and manufacturing of non-polyvinyl chloride infusion sets is much higher than that of polyvinyl chloride infusion sets, which is not conducive to popularization and use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Safe infusion apparatus and preparation method thereof
  • Safe infusion apparatus and preparation method thereof
  • Safe infusion apparatus and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Weigh A1 and B1 materials and add them to the double-layer co-extrusion blow molding unit respectively. The screw diameter of the extruder unit is 40mm, the length-to-diameter ratio is 36, and the head is the center feed of the inner layer and the side feed of the outer layer for co-extrusion. Blow-molded structure. Set the temperature of the feed section of the extruder for material A1 to 150-160°C, the temperature of the compression section to 160-170°C, and the temperature of the metering section to 170-180°C; set the temperature of the feed section of the extruder for material B1 to 140-155°C, The temperature of the compression section is 150-165°C, the temperature of the metering section is 160-175°C; the temperature of the co-extrusion blow molding head is set at 170-180°C.

[0035] After the polyurethane and polyvinyl chloride are dried, add them into the hopper of the polyurethane extruder and the hopper of the polyvinyl chloride extruder of the double-layer co-...

Embodiment 2

[0039] The materials A1 and B2 were weighed and added to the double-layer co-extrusion blow molding unit respectively. The diameter of the screw of the extruder unit was 40mm, and the length-to-diameter ratio was 36. Set the temperature of the feed section of the extruder for material A1 to 150-160°C, the temperature of the compression section to 160-170°C, and the temperature of the metering section to 170-180°C; set the temperature of the feed section of the extruder for material B2 to 140-155°C, The temperature of the compression section is 150-165°C, the temperature of the metering section is 160-175°C; the temperature of the co-extrusion blow molding head is set at 170-180°C. After drying the polyurethane and polyvinyl chloride, add them into the hopper of the polyurethane extruder and the hopper of the polyvinyl chloride extruder of the double-layer co-extrusion blow molding unit at a weight ratio of 1:3, set the polyurethane extruder, vinyl chloride The feeding rate rat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a safe infusion apparatus and a preparation method thereof. The infusion apparatus comprises a dropping funnel and a perfusion tube; wherein, both the dropping funnel and the perfusion tube are made of polyurethane / polyvinyl chloride double-layer composite material; the inner surface layer of the dropping funnel made of the polyurethane / polyvinyl chloride double-layer composite material is a polyurethane layer, and the outer surface layer thereof is a polyvinyl chloride layer. The polyurethane / polyvinyl chloride double-layer composite material is prepared by a co-extrusion blow molding method, and the perfusion tube made of the polyurethane / polyvinyl chloride double-layer composite material is prepared by a co-extrusion method. The safe infusion apparatus can avoid the defect that the polyvinyl chloride perfusion tube absorbs micromolecules such as medicine, plasticizer and the like to pollute liquid medicine, and has the advantages of excellent mechanical property, easy bonding and assembling as well as low raw material cost.

Description

technical field [0001] The invention relates to a medical device, in particular to a safety infusion set and a preparation method. Background technique [0002] Polyvinyl chloride is cheap and has excellent comprehensive properties, and is widely used to make disposable infusion sets. With the extensive and in-depth clinical application and the development of related medical science and technology, it has been found that the polyvinyl chloride material itself has potential safety hazards, and there are also many defects in processing and use performance. A small amount of vinyl chloride monomer will be produced in the production or processing of polyvinyl chloride resin, which has been proved to be a carcinogen. In order to obtain soft polyvinyl chloride products, plasticizers must be used in processing, among which, bis(2-ethylhexyl phthalate) (DEHP) plasticizers are used the most, and such plasticizers will enter the drug liquid, and then enter the human body, endangerin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61M5/14B29C69/00B29C55/28B29C47/20B29C47/92B29C65/72B23P21/00B29C48/32B29C48/92
Inventor 栾世方殷敬华石恒冲
Owner SHANDONG WEIGAO GROUP MEDICAL POLYMER