Restoring method of bent and raised veneer

A veneer and rocker technology, which is used in wood treatment, wood processing appliances, wood treatment details, etc., can solve the problems of long production cycle, high production cost, environmental pollution, etc., and achieves low production cost, short production cycle, and no waste water. The effect of emissions

Active Publication Date: 2009-12-09
ZHEJIANG SHIYOU TIMBER
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a recovery method for sawtooth veneer, which solves the technica

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1: Take oak wood as an example. Use a frame saw to saw the 21mm thick dry oak veneer into 3.5mm thick veneer. Stack the 3.5mm thick oak veneer that has deformed tiles into one layer, and then separate each layer of veneer with spacers After opening, they are piled up in piles with a spacing of 200mm. Then heat and increase the temperature. After the oak veneer temperature rises to 90°C, keep it at 90°C for 45min. Then, let the oak veneer be treated with high temperature and high humidity at 95°C and 98% relative humidity for 50 minutes to make the deformed oak veneer straighten. Finally, the oak veneer is dried for 20 hours at a temperature of 50° C. and a relative humidity of 60% to obtain a dry straight veneer.

Example Embodiment

[0023] Example 2: Take oak wood as an example. Use a frame saw to saw the 21mm thick dry oak veneer into 4.5mm thick veneer, stack the 4.5mm thick veneer of the oak veneer with tile deformation, and stack each 5 pieces into one layer, and then separate each layer of veneer with spacers After opening, they are piled up in piles with a spacing of 280mm. Then heat and increase the temperature. After the oak veneer temperature rises to 100°C, keep it at 100°C for 40 minutes. Then, let the oak veneer be treated with high temperature and high humidity at 100°C and 98% relative humidity for 30 minutes to make the deformed oak veneer straight. Finally, the oak veneer is dried for 20 hours at a temperature of 60°C and a relative humidity of 60% to obtain a dry straight veneer.

Example Embodiment

[0024] Example 3: Take oak wood as an example. Use a frame saw to saw the 21mm thick dry oak veneer into 2.5mm thick veneer, stack 2 pieces of oak veneer with a thickness of 2.5mm with tile deformation into one layer, and then separate each layer of veneer with spacers After opening, they are piled up in piles with a spacing of 100mm. Then heat and increase the temperature. After the oak veneer temperature rises to 70°C, keep it at 70°C for 55 minutes. Then, let the oak veneer be treated with high temperature and high humidity at 75°C and 98% relative humidity for 60 minutes to make the deformed oak veneer straight. Finally, the oak veneer is dried for 10 hours at a temperature of 60°C and a relative humidity of 45% to obtain a dry straight veneer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of wood processing, in particular to a restoring method of a bent and raised veneer. The restoring method comprises the steps of heating, steaming and drying. Compared with the prior art, the restoring method adopts a process, which integrates restoration and straightening with secondary drying, to restore and dry the bent and raised veneer. A high-temperature and high-humidity method is adopted for eliminating the residual deformation inside the width-deformed veneer and drying the veneer which restores the straightness in the conditions of constant temperature and constant humidity. The restoring method has the advantages of short production period, simple process, low production cost, no wood color deepening, no waste water discharge, no environment pollution, strong practicality, and the like.

Description

technical field [0001] The invention relates to the technical field of wood processing, in particular to a method for reusing waste wood. Background technique [0002] Veneer is a surface decorative wood used to produce solid wood composite flooring and furniture. The veneer with a thickness of 2-5mm is usually obtained by sawing the dry board with a frame saw or a multi-blade saw. After the board is dried, there is residual stress inside the board. After the dried board is sawed into veneer by frame saw or multi-blade saw, the outermost two layers of veneer will be deformed due to the mutual restraint and release of each layer. The deformation of tiles brings inconvenience to the subsequent processing and utilization of veneer, and also seriously affects the quality of wood products. For the veneer with severe deformation of the tiles, it can't even be used, resulting in waste of wood and economic losses to the enterprise. [0003] Although there are literature reports o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27K5/00
Inventor 涂登云倪月中潘成锋徐开蒙曹海波王明俊章昕
Owner ZHEJIANG SHIYOU TIMBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap