Process for manufacturing inner-encaustic brick

A manufacturing process and color brick technology, applied in decorative arts, special decorative structures, etc., can solve the problems of uneven distribution of paint attached to the product, large differences in manual production, and low yield, and avoid uneven distribution of glass paint. , The effect of reducing production cost and increasing output

Inactive Publication Date: 2009-12-30
德州振华装饰玻璃有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to overcome the deficiencies of the prior art, the present invention provides a manufacturing process of inner colored bricks to solve the problems caused by the prior...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Taking the production of 46 red inner colored bricks as an example, the temperature is ≥20°C, and the relative air humidity is ≤40%. The ratio of raw material capacity is: glass paint: paint thinner: catalytic sizing agent = 5:3:0.5; specific manufacturing process:

[0014] 1. Paint matching: glass paint: paint thinner: catalytic sizing agent = 5: 3: 0.5 = 325ml: 195ml: 32ml = 552ml; the mixed solution of 552ml can be used to produce 46 inner colored bricks.

[0015] When mixing paint, the measuring cup should be cleaned to ensure that there is no dust, impurities and waste paint.

[0016] Addition of glass varnish - glass varnish is the basic coloring raw material, when opening the lacquer box, care should be taken to prevent sundries and dust from falling in, so as not to affect the purity. Place the measuring cup horizontally on the horizontal surface, and paint 325ml of red glass into the measuring cup according to the specified proportion.

[0017] The addition of...

Embodiment 2

[0027] Take the production of 46 red inner colored bricks as an example, the ratio of raw material capacity for the temperature below 20°C and the relative air humidity above 40%:

[0028] 1. Paint matching: glass paint: paint thinner: catalytic sizing agent=5: 2: 0.5=370ml: 148ml: 42ml=560ml, the mixed solution of 560ml can be used to produce 46 interior colored bricks.

[0029] When mixing paint, the measuring cup should be cleaned to ensure that there is no dust, impurities and waste paint.

[0030] Addition of glass varnish - glass varnish is the basic coloring raw material, when opening the lacquer box, care should be taken to prevent sundries and dust from falling in, so as not to affect the purity. Place the measuring cup horizontally on the horizontal surface, and paint 370ml of red glass into the measuring cup according to the specified proportion.

[0031] The addition of paint thinner-thinner acts as a thinner to dilute and blend. Pour the prepared 148ml thinner i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a process for manufacturing an inner-encaustic brick, and relates to a method for manufacturing a building material. The process is characterized in that: a flexible process flow is adopted, the blending ratio of the raw materials depends on air temperature and air humidity; when the air temperature is less than or equal to 20 DEG C and the relative air humidity is more than or equal to 40 percent, the blending ratio of glass paint to paint thinner to catalytic type shaping agent is 4.5-5.5:2.5-3.5:0.4-0.6; and when the air temperature is more than or equal to 20 DEG C and the relative air humidity is less than or equal to 40 percent, the blending ratio of glass paint to paint thinner to catalytic type shaping agent is 4.5-55:2-3:0.4-0.6. The manufacturing process mainly comprises the following steps of paint preparation, filling, annealing, air blowing, paint spraying and finished product. The process has the advantages of greatly lowering labor intensity of workers, improving the output of the inner-encaustic brick by nearly 2 to 3 times, saving manual manufacturing time, lowering production cost, solving the problems of unevenly distribution of the glass paint on the inner surface of the glass brick and wet paint surface existing in the manual manufacturing process, and further improving product quality.

Description

technical field [0001] The invention relates to a method for manufacturing building materials. Background technique [0002] As a new type of glass brick product in the glass brick industry, the inner color brick can change the color at will compared with changing the color of the raw material through the kiln glass process. There are various kinds of inner colored bricks, which belong to handicraft products, but the manual production has the disadvantages of low output, low efficiency and high cost. In the production process, a lot of production time will be wasted in the hand-bricking process and blowing process. The manufacturing process is immature, and various external conditions cannot be grasped. In addition, the glass paint adheres unevenly to the inner surface during the hand-made process, resulting in a high yield rate. Low, low output, high cost. Contents of the invention [0003] In order to overcome the deficiencies of the prior art, the present invention pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B44C5/04C03C17/00C03C25/00
Inventor 张满营李勇刘景柱李晓东胡广海邢化亭卢伟董国竹
Owner 德州振华装饰玻璃有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap