Energy-saving high strength aramid fiber conveyer belt and preparation method thereof

A conveyor belt and aramid fiber technology, which is applied in the energy-saving high-strength aramid fiber conveyor belt and its preparation, and in the field of long-distance material transportation, can solve problems such as longitudinal tearing, complicated joints, and easy corrosion, and achieve reduced diameter, chemical Good stability and anti-corrosion effect

Inactive Publication Date: 2013-02-27
WUXI BOTON TECH CO LTD +1
View PDF4 Cites 72 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the process of use, the steel cord conveyor belt is criticized by the user unit due to its heavy weigh

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Energy-saving high strength aramid fiber conveyer belt and preparation method thereof
  • Energy-saving high strength aramid fiber conveyer belt and preparation method thereof
  • Energy-saving high strength aramid fiber conveyer belt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Embodiment 1 DP1600*2 (8+4) aramid conveyor belt

[0050] (1) Preparation of adhesive glue: Take 30 parts by mass of natural rubber (SMR10) and 70 parts by mass of styrene-butadiene rubber (SBR1502) in an internal mixer for 2 minutes, and then add active agent: zinc oxide in parts by mass 5. 2 parts by mass of stearic acid; antiaging agent: 1 part by mass of 4010NA, 1 part by mass of RD; tackifier: 1 part by mass of RA, 1 part by mass of BN-1; reinforcing agent: 20 parts by mass of carbon black N330, gas phase 20 parts by mass of French silica; plasticizer: 6 parts by mass of aromatic oil, and one-stage mixing. After parking for 12 hours, add 2 parts by mass of sulfur and 1.5 parts by mass of accelerator CZ on the open mill for two-stage mixing, and knead for 5 minutes at 80°C, and extrude the compound after the second-stage mixing on the extruder sheet to obtain an adhesive glue with a thickness of 0.8mm.

[0051] (2) Preparation of cover rubber: Take 40 parts by mas...

Embodiment 2

[0074] Embodiment 2 The preparation method of energy-saving high-strength aramid conveyor belt, the formula ratio is as follows by weight:

[0075] (1) Preparation of adhesive glue: Take 60 parts of natural rubber and synthetic rubber to mix the rubber matrix: 25 parts of butadiene rubber and 15 parts of neoprene rubber in the internal mixer for 5 minutes, and then add the active agent stearic acid 10 Parts, anti-aging agent: 1 part of RD, 2 parts of MC, 6 parts of tackifier terpene resin, 30 parts of reinforcing agent clay, 10 parts of calcium carbonate and 2 parts of plasticizer aromatic oil, mix well and place in a mixer at 70°C Mix for 3 minutes to obtain a first-stage mixed rubber, then add 0.5 parts of vulcanizing agent sulfur, 0.2 parts of accelerator DM, and 2 parts of TMTD for second-stage mixing, and mix for 3 minutes at 90 ° C to prepare the rubber compound after the second-stage mixing Sheet adhesive film;

[0076](2) Preparation of cover rubber: Take 80 parts of ...

Embodiment 3

[0080] The preparation method of the energy-saving high-strength aramid conveyor belt is characterized in that the formula ratio is as follows in parts by weight:

[0081] (1) Preparation of adhesive glue: Take 90 parts of natural rubber and mix 10 parts of rubber base nitrile rubber with synthetic rubber, and banbury in an internal mixer for 10 minutes, and then add active agents: 2 parts of zinc oxide and 3 parts of stearic acid , 1 part of anti-aging agent RD, 3 parts of tackifier petroleum-based resin, 70 parts of reinforcing agent clay and 8 parts of plasticizer aromatic oil, after mixing evenly, knead in a mixer at 65 ° C for 4 minutes to obtain a mixed rubber. Then add 5 parts of vulcanizing agent sulfur and 4.0 parts of accelerator CZ for second-stage mixing, and knead at 95°C for 2 minutes, and make the rubber material after the second-stage mixing into a sheet-shaped adhesive film;

[0082] (2) Preparation of cover rubber: Take 70 parts of natural rubber and syntheti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to an energy-saving high strength aramid fiber conveyer belt and a preparation method thereof. The conveyer belt is composed of a skeleton layer, adhesive glue and an upper-lower cover adhesive laminated structure. Firstly, the skeleton layer employs aramid fiber canvas after dipping treatment to replace a conventional steel wire rope, so that the problems of large weight of the steel wire rope which brings much inconvenience for processes of shaping, installing, maintaining and the like is solved. Secondly, the aramid fiber canvas has structure in broadwise direction, has excellent anti-tear and anti-impact performances, so that phenomena of longitudinal tear and the like of the steel wire rope conveyer belt cab be prevented. Compared with a conventional steel wire rope high strength conveyer belt, the energy-saving high strength aramid fiber conveyer belt has high strength, good corrosion resistance, wear resistance and impact and fatigue resistance, and greatly reduce the weight and thickness of the conveyor belt, so that conveying power energy consumption is saved. The energy-saving high strength aramid fiber conveyer belt is expected to have longer service life and better energy-saving and environment-friendly properties, and is particularly suitable for long-distance material conveyance in industries such as coal mine, metallurgy, mine, etc.

Description

technical field [0001] The invention relates to an energy-saving high-strength aramid conveyor belt and a preparation method thereof, which is especially suitable for long-distance material transportation in industries such as coal mines, metallurgy, and mines, and belongs to the technical field of rubber products. Background technique [0002] Rubber conveyor belt is the second largest category of important rubber products after tires, and belongs to the field of petrochemical industry. High-performance conveyor belts are mainly used in key national industries such as coal, metallurgy, building materials, coke, and power generation that support national economic and social development, and the annual growth rate of demand exceeds 25%. my country is the world's largest producer of conveyor belts, but foreign products are still monopolized in high-end application fields and high-end customer groups, earning huge profits with high added value. With the continuous development ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08L9/06C08L9/00C08L11/00C08L23/16C08L9/02C09J107/00C09J109/06C09J109/00C09J111/00C09J123/16C09J109/02B65G15/34B29C35/02B32B37/12B32B27/02
Inventor 张立群萨日娜田明王文才吴建国袁佳春严岩
Owner WUXI BOTON TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap