X120 pipeline steel with low crack sensitivity and high toughness and manufacturing method thereof
A manufacturing method and sensitive technology, applied in the field of low crack sensitivity and high toughness X120 pipeline steel and its manufacturing field, can solve the problems of strict production process control requirements, high alloy composition design of pipeline steel, unfavorable mass production, etc. Moderate process requirements, favorable for large-scale production, and low alloy costs
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0041] The present invention will be further described below: the ingredients and weight percentages of the examples are shown in Table 1; production process:
[0042] 1) Smelting: hot metal desulfurization-converter top and bottom combined blowing-ladle furnace treatment-vacuum (Si-Ca) treatment-pouring into slab;
[0043] 2) Heating the continuous casting slab to 1100~1250℃;
[0044] 3) Carry out rough rolling: control the end temperature of rough rolling at 1000~1100℃;
[0045] 4) Perform finishing rolling: control the finishing temperature of finishing rolling at 800~900℃;
[0046] 5) The steel plate stays for 10 to 60 seconds;
[0047] 6) Cooling: The cooling rate is controlled at 10-30°C / sec, and the final cooling temperature is controlled at ≤450°C.
[0048] The specific process parameters are shown in Table 2; the mechanical properties of the examples are shown in Table 3.
[0049] Table 1 The chemical composition of Examples 1 to 5 (wt%)
[0050] C
[0051]
[0052] Table 2 Ro...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap