Water-based PU Nubuck high-temperature foamex for synthetic leather

A high-temperature foaming, synthetic leather technology, applied in fiber processing, textiles and papermaking, etc., can solve problems such as poor viscosity, stability, hand feel and other comprehensive effects, poor synthetic leather feel, easy to pollute the environment, etc. Excellent comprehensive effect, unique effect, good air permeability

Inactive Publication Date: 2010-05-12
JIANGSU BAOZE POLYMER MATERIAL
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. The organic solvent contained in the solvent-type Yangbuck high-temperature foaming resin will cause the bottom layer of synthetic leather or artificial leather to dissolve, and the treated synthetic leather will not feel good;
[0005] 2. The organic solvent contained in solvent-type Yangba high-temperature foaming

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] 1. The water-based PU Yangbuck high-temperature foaming resin for synthetic leather is composed of the following raw materials: 100 kg of water-based polyurethane (30% solid content), 80 kg of ordinary tap water, 3 kg of high-temperature Yangbuck powder, 10 kg of water-based polyurethane thickener, organic 1 kg of silicon defoamer, 3 kg of silicone leveling agent.

[0028] 2. The preparation method of the water-based PU Yangbuck high-temperature foaming resin for synthetic leather of the present invention is as follows:

[0029] ① Proportionally select 100 kg of water-based polyurethane (30% solid content), 80 kg of ordinary tap water, 1 kg of silicone defoamer, and 3 kg of silicone leveling agent, mix and stir;

[0030] ② Take 3 kg of high-temperature yangbuck powder and add the mixture obtained in step ① while stirring, and filter through 200 mesh;

[0031] ③ Take the mixture obtained in step ② and filter, add 10 kg of water-based polyurethane thickener in proportion...

Embodiment 2

[0036] 1. The water-based PU Yangbuck high-temperature foaming resin for synthetic leather is composed of the following raw materials: 80 kg of water-based polyurethane (30% solid content), 700 kg of ordinary tap water, 2.5 kg of high-temperature Yangbuck powder, 9 kg of water-based polyurethane thickener, organic 1 kg of silicon defoamer, 3 kg of silicone leveling agent.

[0037] 2. The preparation method of the water-based PU Yangbuck high-temperature foaming resin for synthetic leather of the present invention is as follows:

[0038] ① Proportionally select 80 kg of water-based polyurethane (30% solid content), 70 kg of ordinary tap water, 1 kg of silicone defoamer, and 3 kg of silicone leveling agent, mix and stir;

[0039] ②Take 2.5 kg of high-temperature yangbuck powder and add the mixture obtained in step ① while stirring, and filter through 200 mesh;

[0040] ③ Take the mixture obtained in step ② and filter, add 9 kg of water-based polyurethane thickener in proportion...

Embodiment 3

[0046] 1. The water-based PU Yangbuck high-temperature foaming resin for synthetic leather is composed of the following raw materials: 65 kg of water-based polyurethane (30% solid content), 55 kg of ordinary tap water, 2.5 kg of high-temperature Yangbuck powder, 5 kg of water-based polyurethane thickener, organic 1 kg of silicon defoamer, 2.5 kg of silicone leveling agent.

[0047] 2. The preparation method of the water-based PU Yangbuck high-temperature foaming resin for synthetic leather of the present invention is as follows:

[0048] ① Proportionally select 65 kg of water-based polyurethane (30% solid content), 55 kg of ordinary tap water, 1 kg of silicone defoamer, 2.5 kg of silicone leveling agent, mix and stir;

[0049] ②Take 2.5 kg of high-temperature yangbuck powder and add the mixture obtained in step ① while stirring, and filter through 200 mesh;

[0050] ③ Take the mixture obtained in step ② and filter, add 5 kg of water-based polyurethane thickener in proportion,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a water-based PU Nubuck high-temperature foamex for synthetic leather, which comprises the following materials by weight percent: 30 to 40 percent of water-based polyurethane resin, 40 to 50 percent of water, 2 to 10 percent of high-temperature Nubuck foam powder, 2 to 5 percent of organic silicon flatting agent, 2 to 5 percent of organic silicon foam killer, and 0.5 to 2 percent of water-based polyurethane thickening agent. For the water-based PU Nubuck high-temperature foamex for the synthetic leather, the mixture ratio of the components is scientific and reasonable, and the components are coordinated with each other and act together. The Nubuck high-temperature foamex for synthetic leather has the advantages of good film reforming property, firm bonding and solvent resistance, cold resistance, hydrolysis resistance and thermosenescence resistance of coating. By adopting the finished product of the synthetic leather, the surface of which is treated by water-based PU Nubuck high-temperature foamex, the original effect of the leather surface is not affected. After the leather surface is treated by the PU Nubuck high-temperature foamex, Nubuck leather is produced through high-temperature foaming, the effect is unique, the texture of the synthetic leather is fine and smooth, and the synthetic leather has good comprehensive effects of good air permeability, good hand feel, water resistance, cohesiveness and the like.

Description

technical field [0001] The invention relates to a water-based PU Yangbuck high-temperature foaming resin for synthetic leather, in particular to a water-based PU Yangbuck high-temperature foaming resin for synthetic leather used in the back-stage process of synthetic leather. Background technique [0002] With the improvement of people's living standards, people are gradually pursuing high-quality daily products, and the demand for leather products is increasing. With the enhancement of animal protection awareness, animal leather can no longer meet people's needs. At present, synthetic leather products have gradually become a popular trend in the future. Synthetic leather has been widely used in the production of luggage, clothing, footwear and other products. The base fabric of PU leather is canvas PU material with good tensile strength. In addition to being coated on the base fabric In addition to the upper surface, the base fabric can also be included in the middle, so th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/564D06M13/50D06N3/14
Inventor 时云刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products