Super high-temperature resistant coating and preparation method thereof

A high-temperature-resistant coating, super technology, applied in anti-corrosion coatings, fire-resistant coatings, coatings, etc., can solve the problems of poor temperature resistance and poor corrosion resistance of heat-resistant coatings, and achieve excellent temperature resistance and simple construction.

Inactive Publication Date: 2010-06-23
SHANGHAI DATONG HIGH TECH MATERIALS
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, with the continuous adjustment and updating of production processes in various chemical plants, oil refineries, and power plants, various devices such as: high-temperature boilers, exhaust devices, chimneys, etc. have higher and higher requirements for various functions of heat-resistant coatings. It turns out that the temperature range of traditional heat-resistant coatings is usually up to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] Example 1

[0032] A preparation method of super high temperature resistant coating, the method includes the following process steps:

[0033] (1) Put 40kg of silicon modified resin and 15kg of solvent xylene into the kettle for high temperature reaction and hydrolysis at 500℃, and polymerize for 24 hours to make semi-finished products;

[0034] (2) Put the finished semi-finished product into the equipment, then add 20kg of coated metal powder, 10kg of additive hydrogenated castor oil, 5kg of solvent xylene and stir (600rpm) for 35 minutes;

[0035] (3) Leave it to stand for 12 hours to prepare super high temperature resistant coatings and test indicators;

[0036] (4) After being sent to the quality inspection department, the package will be put into storage.

Example Embodiment

[0037] Example 2

[0038] A preparation method of super high temperature resistant coating, the method includes the following process steps:

[0039] (1) Add 50kg of silicon modified resin and 15kg of solvent butanol into the kettle for high temperature reaction and hydrolysis at 700℃, and polymerize for 24 hours to make semi-finished products;

[0040] (2) Add the semi-finished product to the equipment, then add 30 kg of coated metal powder, 10 kg of additive organosilane, and 5 kg of solvent butanol, then stir (600-750 rpm) for 35 minutes;

[0041] (3) Leave it to stand for 12 hours to prepare super high temperature resistant coatings and test indicators;

[0042] (4) After being sent to the quality inspection department, the package will be put into storage.

Example Embodiment

[0043] Example 3

[0044] A preparation method of super high temperature resistant coating, the method includes the following process steps:

[0045] (1) Add 60kg of silicone modified resin and 15kg of solvent into the kettle for high temperature reaction and hydrolysis, and polymerize for 24 hours to make semi-finished products;

[0046] (2) Add the semi-finished product to the equipment, then add 45kg of coated metal powder, 15kg of additives, and 5kg of solvent, and then stir (600 rpm) for 35 minutes;

[0047] (3) Let stand for 24 hours to prepare super high temperature resistant coating, test index;

[0048] (4) After being sent to the quality inspection department, the package will be put into storage.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a super high-temperature resistant coating and a preparation method thereof. The coating comprises the following components in part by weight: 40 to 60 parts of organosilicon modified resin, 20 to 45 parts of coated metal powder, 10 to 15 parts of additive and 10 to 25 parts of solvent. Compared with the prior art, the super high-temperature resistant coating can protect a metal surface from being corroded in the operating state and high and low temperature alternating state of ultrahigh-temperature equipment, and has the advantages that: (1) the coating has excellent temperature-resistant performance and can be used at the temperature of higher than 800 DEG C for a long time; (2) the coating has the extremely good corrosion resistance on the premise of having excellent temperature tolerance; (3) the phenomena such as cracking, rusting and the like cannot be generated when an ambient temperature suddenly drops; and (4) priming paint is the same as the coating with easy construction.

Description

technical field [0001] The invention relates to coatings, in particular to a super high temperature resistant coating and a preparation method thereof. Background technique [0002] At present, with the continuous adjustment and updating of production processes in various chemical plants, oil refineries, and power plants, various devices such as: high-temperature boilers, exhaust devices, chimneys, etc. have higher and higher requirements for various functions of heat-resistant coatings. It turns out that the temperature range of traditional heat-resistant coatings is usually up to 700 ° C, and the temperature resistance is poor. When the high-temperature device returns to normal temperature, the defect of poor corrosion resistance of the heat-resistant coating will be exposed; therefore, the market urgently needs a A temperature-resistant anti-corrosion coating with a temperature resistance of about 800°C, good temperature denaturation resistance and excellent anti-corrosio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D183/04C09D5/18C09D5/10
Inventor 李成章杨志英
Owner SHANGHAI DATONG HIGH TECH MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap