Grease used for metal fastener

A technology for metal fasteners and grease, applied in the field of grease, can solve the problems to be further improved, and achieve the effects of prolonging the anti-corrosion and anti-rust period, excellent sealing and improving the anti-rust performance.

Inactive Publication Date: 2010-08-18
成都蜀光石油化学有限公司
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent ZL03104974.5 discloses a kind of protective grease, which fills the domestic gap in this technology, but the protective grease uses components that have adverse effects on the environment such as petroleum pitch, black graphite, and diphenylamine , it needs to be improved, and its rust resistance, oxidation resistance, and ability to resist rain erosion also need to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Grease used for metal fastener
  • Grease used for metal fastener
  • Grease used for metal fastener

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] In this embodiment, the weight percent content of each component of base grease, film-forming agent, anti-oxidant anticorrosion agent, rust preventive agent and solid filler is shown in Table 2, wherein:

[0043] The base fat is saponified from the following raw materials: 8.5wt% lauryl hydroxystearic acid, 2.5wt% stearic acid, 2.5wt% lithium hydroxide monohydrate, and the balance is base oil;

[0044] The film forming agent is composed of 10 parts of ethylene propylene copolymer and 0.6 parts of epoxy resin E44;

[0045] The anti-oxidation and anti-corrosion component agent is octyl / butyl diphenylamine;

[0046] The antirust agent is composed of 4.5 parts of barium petroleum sulfonate (T701), 0.5 parts of lanolin magnesium soap, and 0.1 part of benzotriazole (T706);

[0047] The solid filler consists of 5.0 parts of mica powder, 10.0 parts of talc powder, and 1.0 part of glass microspheres;

[0048] The ointment of this embodiment has a beige bright and uniform appea...

Embodiment 2

[0050] In this embodiment, the weight percent content of each component of base grease, film-forming agent, anti-oxidant anticorrosion agent, rust preventive agent and solid filler is shown in Table 2, wherein:

[0051] The base grease is formed by saponification reaction of the following raw materials: 7.0 wt% lauryl hydroxystearic acid, 4.0 wt% stearic acid, 2.5 wt% lithium hydroxide monohydrate, and base oil as the balance.

[0052] The film forming agent is composed of 15 parts of ethylene propylene copolymer and 2 parts of epoxy resin E44;

[0053] The anti-oxidation and anti-corrosion component is octyl / butyl diphenylamine;

[0054] The antirust agent is composed of 4.5 parts of barium dinonylnaphthalenesulfonate (T705), 2.0 parts of lanolin magnesium soap, and 0.1 part of benzotriazole (T706);

[0055] The solid filler consists of 10.0 parts of mica powder, 15.0 parts of light calcium carbonate, and 1.0 part of glass microspheres;

[0056] The ointment of this embodim...

Embodiment 3

[0058] In this embodiment, the weight percent content of each component of base grease, film-forming agent, anti-oxidant anticorrosion agent, rust preventive agent and solid filler is shown in Table 2, wherein:

[0059] The base grease is formed by the saponification reaction of the following raw materials: 9.0wt% lauryl hydroxystearic acid, 3.5wt% stearic acid, 1.6wt% lithium hydroxide monohydrate, 0.4wt% lime powder, and base oil as the balance;

[0060] The film forming agent is composed of 10.0 parts of ethylene propylene copolymer and 2.0 parts of polyisobutylene;

[0061] The antioxidant preservative is octyl / butyl diphenylamine;

[0062] The antirust agent is composed of 4.5 parts of barium dinonylnaphthalenesulfonate (T705), 0.5 parts of lanolin magnesium soap, and 0.1 part of benzotriazole (T706);

[0063] The solid filler consists of 5.0 parts of mica powder, 10.0 parts of talc powder, and 1.0 part of plastic microspheres.

[0064] The ointment of this embodiment h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses grease used for a metal fastener, which is prepared from the following components in percentage by weight ( in percentage by total weight of the grease): 50.0 to 90.0 percent of basic grease, 1.5 to 20.0 percent of film-forming agent, 0.1 to 1.0 percent of anti-oxidation preservative, 5.1 to 8.3 percent of anti-rust agent and 2.5 to 26.0 percent of solid stuffing. The grease has higher oxidation resistance, higher corrosion and rust resistance, better water resistance, more excellent sealing property, better pressure resistance, better adhesivity, more environment-friendly suitability, convenient brushing and injection and stable structure and is not easy to generate swelling action on protected nonmetal assorted components. The grease can be largely applied to thespeed acceleration of the trunk line of the railway ballastless track.

Description

technical field [0001] The present invention relates to a kind of grease, in particular to a kind of grease used for antirust, anticorrosion and sealing of metal fasteners. Anti-rust, anti-corrosion and sealing of outdoor crane fastening fasteners, construction fasteners, metallurgical fasteners, oil pipelines and other equipment components (such as spikes, bolts, threads, etc.). Background technique [0002] The multi-series concrete sleepers of my country's railways are laid, and the fasteners, sleepers, and switch sleepers are connected by sulfur anchorage. The protection of this kind of track fastening fasteners is traditionally made of calcium-based grease (butter) for anti-corrosion protection. There are also Use waste engine oil or mixed with asphalt to heat, or grease that has not been verified and strictly inspected for anti-corrosion protection. In recent years, my country's railway construction has developed rapidly, and the speed of railways has been increased si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M161/00C10M125/00C10N40/34C10N50/10C10N30/12
Inventor 夏位松张绪伟王洪刚
Owner 成都蜀光石油化学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap