Low-carbon ultra-deep punching cold-rolling steel sheet and production method thereof

A technology of cold-rolled steel plate and production method, which is applied in the field of iron and steel smelting and rolling, and can solve the problems of less research on aluminum-killed steel for ultra-deep drawing, low production efficiency, and high production cost, so as to improve the cleanliness of molten steel and facilitate the production process , the effect of reducing the C content

Inactive Publication Date: 2010-12-15
TANGSHAN GUOFENG IRON & STEEL
View PDF8 Cites 43 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Cold-rolled steel for ultra-deep drawing generally refers to ultra-low carbon interstitial atom-free steel (IF steel), which is obtained by controlling the C and N content in the alloy and adding alloy elements such as Nb and Ti. Due to the lower C and N content , and contains trace elements such as Nb and Ti, its production cost is relatively high, and this steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The present invention is described in detail below in conjunction with embodiment.

[0022] In the following examples, the ZSP production line is 309.1m long, the pickling and cold rolling line is 250m long, the finished coils have a specification of (0.5-1.5)×(900-1300)×C, and the coil weight is about 16 tons.

[0023] The low-carbon ultra-deep drawn cold-rolled steel sheet given in this example has the following chemical composition by weight percentage: C: 0.01%, Si: 0.015%, Mn: 0.16%, P: 0.015%, S: 0.009%, Als : 0.033%; molten steel temperature 1610°C. Its production method is carried out as follows:

[0024] 1. Steelmaking: The steelmaking furnace adopts a converter with a capacity of 120 tons, with a tapping capacity of 125 tons and a tapping temperature of 1655°C. After the molten iron is desulfurized and slag removed, it goes into the converter to smelt the molten steel. The molten steel from the steelmaking furnace is refined in the LF and RH refining furnace...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a low-carbon ultra-deep punching cold-rolling steel sheet and a production method thereof, belonging to the technical field of steel smelting and calendaring. The steel sheet comprises the following chemical components in weigh percentage: 0.006%-0.012% of C, 0.15%-0.20% of Mn, 0.030%-0.070% of Als, 0.015% of Si or less, 0.012% of P or less, 0.010% of S oe less, not more than 0.0030% of N or less, 0.0035% percent of O or less and the balance of Fe and inevitable impurities. Based on a ZSP sheet blank continuous casting and rolling process, the production method comprises the following working procedures of steel smelting, continuous casting, heating, hot rolling, cooling and curling, acid washing and cold rolling, and annealing and flattening. The steel sheet has excellent mechanical property and stamping forming property and simple chemical component and is suitable for punching products needing ultra-deep punching, such as fuel tank caps of automobiles; and the production method has the advantages of easy operation, low production cost, energy saving and consumption reduction and is beneficial to generalization and application.

Description

technical field [0001] The invention relates to a low-carbon ultra-deep drawn cold-rolled steel plate and a production method thereof, belonging to the technical field of iron and steel smelting and rolling. Background technique [0002] In recent years, with the rapid development of the automobile, home appliance and machinery industries and the intensification of competition in the steel industry, the demand for high value-added, high-quality, high-tech and low-cost varieties of steel is increasing. The development and manufacture of ultra-deep drawing steel can be Provide excellent manufacturing raw materials for related industries, and at the same time create good economic benefits for iron and steel enterprises. [0003] Cold-rolled steel for ultra-deep drawing generally refers to ultra-low carbon interstitial atom-free steel (IF steel), which is obtained by controlling the C and N content in the alloy and adding alloy elements such as Nb and Ti. Due to the lower C and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/04C22C33/04C21D8/04
Inventor 焦景民孟威
Owner TANGSHAN GUOFENG IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap