Nonmetallic heating filament and preparation method thereof

A heating wire and non-metal technology, applied in the field of non-metal heating wire and its preparation, can solve the problem of high cost of metal heating wire, and achieve the effect of obvious energy saving, low operating cost and shielding electromagnetic radiation.

Inactive Publication Date: 2011-01-05
韩奎
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, because the metal heating wire is relatively expensive, people expect a new non-metallic heating wire to replace the metal heating wire to achieve the effect of heating and heat preservation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] According to the following components by weight, carbon composite conductive carbon paste is prepared: 1-2 parts of acrylic resin, 1-2 parts of polyurethane resin, 0.5-1 part of carbon black, 0.5-1 part of graphite, 0.1 part of leveling agent and defoaming agent dose 0.1 part.

[0027] Use a pay-off machine or a pay-off bracket to pay off the polyester-cotton yarn. When paying off, ensure that the line has a certain resistance to ensure the straightness of the line and the uniformity of the line speed.

[0028] Immerse the polyester-cotton yarn into the carbon-composite conductive carbon paste through the crimping wheel, so that the polyester-cotton yarn is immersed and hung with sufficient conductive carbon paste, and passes through a mold hole, the diameter of which is 0.38-0.80mm.

[0029] Put the dipped and shaped wire into a drying oven for drying and heating to solidify the carbon-composite conductive carbon paste to form a stable shell film. The drying temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nonmetallic heating filament and a preparation method thereof. The nonmetallic heating filament is made by taking a polyester / cotton yarn as a base material, coating a layer of a heating conductive polymeric compound coating on the external surface of the base material and finally drying the coating, wherein, a heating conductive polymeric compound is carbon composite conductive carbon paste, and the carbon composite conductive carbon paste comprises the following components in parts by weight: 1-2 parts of acrylic resin, 1-2 parts of polyurethane resin, 0.5-1 part of carbon black, 0.5-1 part of graphite, 0.1 part of a levelling agent and 0.1 part of a defoaming agent. The preparation method of the nonmetallic heating filament comprises the following steps: paying-off the yarn, soaking the yarn into the paste, shaping, drying, measuring resistance and taking-up the yarn. In the invention, the heating conductive polymeric compound is taken as a heating material and voltage is added to two ends of the heating conductive polymeric compound so that the heating conductive polymeric compound can radiate energy outwards in a far infrared manner, and a far infrared ray has thermal action, thus achieving the heating purpose.

Description

technical field [0001] The invention relates to a non-metal heating wire and a preparation method thereof. Background technique [0002] We know that the principle of metal heating is: after the metal wire is energized, it generates heat due to its own resistance, and then dissipates the heat in the form of heat conduction. [0003] Metal heating wires are widely used in China. For example, the vast majority of existing electric blankets are made of metal heating wires, and their quality assurance period is generally ten years. [0004] The metal heating wire is relatively hard, and it will be broken if it is bent many times during use. On the one hand, it will affect the use, and on the other hand, it will easily cause safety hazards. This requires the user to be very careful during use to avoid bending the metal heating wire many times. [0005] Since the civil electricity in our country is 50Hz alternating current, a periodically changing electromagnetic wave field will...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H05B3/14
Inventor 韩奎
Owner 韩奎
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products