Powder paint with high surface harness and decoration

A powder coating and decorative technology, applied in the direction of powder coating, polyester coating, epoxy resin coating, etc., can solve the problem of limited anti-scratch effect

Active Publication Date: 2011-01-12
黄山华佳表面科技有限公司
View PDF16 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the other hand, from a technical point of view, simply using the above-mentioned mixed wax as an additive to improve the anti-scratch effect is also quite limited, so it is expected to provide high surface hardness and decorative performance, good surface scratch resistance, economy or its coating. Powder coatings where surface modifiers are commercially available are extremely desirable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Powder paint with high surface harness and decoration
  • Powder paint with high surface harness and decoration
  • Powder paint with high surface harness and decoration

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0099] 100 parts by weight of epoxy resin (E-12), 100 parts by weight of polyester resin SYP4500 (Huangshan Yongjia Sanli product, AV about 75mgKOH / g), 3 parts by weight of leveling agent Resiflow P67 (Estron), 78.1 parts by weight of BaSO 4 Filler, 1.5 parts by weight of benzoin, 15 parts by weight of FR921-1 (high molecular weight PVDF, particle size about 50 μm, Shanghai Sanaifu Company) and 2.4 parts by weight of carbon black were placed in a plastic bag and mixed manually for 3-5 minutes. Then add it into a twin-screw test extruder to melt and homogenize, tablet, cool and grind into fine powder, and sieve through 180 mesh. Electrostatic spraying on degreased cold-rolled steel plate, curing at 180°C / 15 minutes. Then test according to the above test method, the specific results are listed in Table 1.

example 2-10 and comparative example 11

[0101] Repeat Example 1, but use different fluorocarbon resins or their combinations and the combination of characteristic wear-resistant inorganic fillers to replace the same components in Example 1; as Comparative Example 11, completely use 93.1 parts by weight of BaSO 4 The various additive groups in Substitution Example 1 were compared with each other, and the specific results are also listed in Table 1.

example 12

[0103] 186 parts by weight of polyester resin CC2440-2 (Cytec, AV about 34mgKOH / g), 14 parts by weight of TGIC, 3 parts by weight of leveling agent Resiflow P67 (Estron), 78.1 parts by weight of BaSO 4Filler, 1.5 parts by weight of benzoin, 15 parts by weight of FR921-1 (high molecular weight PVDF, particle size about 50 μm, Shanghai Sanaifu Company) and 2.4 parts by weight of carbon black were placed in a plastic bag and mixed manually for 3-5 minutes. Then add a twin-screw test extruder to melt and homogenize, tablet, cool and grind into fine powder, and sieve through 180 mesh. Electrostatic spraying on degreased cold-rolled steel plate, curing at 200°C / 10 minutes. Then test according to the above test method, and the specific results are listed in Table 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
acid valueaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses powder paint with high surface harness and decoration. The powder paint contains one or more 100% fluorocarbon resin by weight, one or more glass microspheres and ceramic microballons as well as a characteristic inorganic filler taking nephelinite as a main component. Compared with the prior art, the fluorocarbon resin of the invention has good compatibility with a film-forming resin, and the coating embodies excellent decorative effect.

Description

technical field [0001] This invention relates to powder coating compositions. More precisely, the present invention relates to a powder coating composition having high surface hardness and decorative properties, using a special 100% content of fluorocarbon resin, a characteristic wear-resistant inorganic filler or a combination thereof as a coating surface hardening material; Furthermore, the present invention is also related to the application of this special fluorocarbon resin and the powder coating composition formed therefrom. Background technique [0002] Thermosetting powder coating is an environmentally friendly coating with no or very little solvent and volatile emissions, especially in today's increasingly stringent VOC (Volatile Organic Compounds, volatile organic compounds) emission standards, it is of great significance and market share is increasing year by year. [0003] Thermosetting powder coatings are mainly composed of functional film-forming resin materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D167/00C09D133/00C09D127/18C09D127/12C09D127/14C09D127/16C09D127/20C09D5/03C09D7/12
Inventor 吴正亮吴洪波童乃斌
Owner 黄山华佳表面科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap