Silver plating method for glass mirror

A glass mirror and silver-plating technology, which is applied in the field of silver plating, can solve the problems of reducing the reflectivity of the glass mirror and reducing the compactness of the silver layer

Active Publication Date: 2012-12-19
江阴市京澄玻璃有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the silver plating method of glass mirrors is as follows: glass cleaning → sensitization → hypersensitization → silver plating → passivation → secondary passivation → primer coating → primer baking → surface coating → air cooling → pickling Surface → display cleaning → finished product; the silver plating process adopts the method of one-time silver plating, that is, the reduction reaction of silver nitrate is carried out with the reducing solution, and the reaction temperature is 28-30°C; currently, the silver plating layer of the glass mirror is required to be made The reflectivity of the glass mirror is high and the thickness of the silver layer is increased at the same time; but to improve the reflectivity of the glass mirror, the compactness of the silver layer will be improved, which can only be achieved by reducing the reaction rate of the reaction solution during silver plating, but the reaction rate of the reaction solution is reduced Simultaneously can reduce the conversion rate of silver nitrate in the reaction solution and the thickness of silver layer; On the contrary will improve the silver layer thickness of glass mirror only by improving the reaction speed of reaction solution when silver plating, thus improve the conversion rate and silver layer of silver nitrate in the reaction solution The thickness of the silver layer, but it will reduce the density of the silver layer, thereby reducing the reflectivity of the glass mirror

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] In the following examples, the low-speed reaction reducing solution is Ma2000 low-speed reaction reducing solution from Valspar Company in Germany, and the high-speed reaction reducing solution is 747 high-speed reaction reducing solution from DR.ING (.Dring).schmitt Company in Germany.

[0010] Example 1: To produce a silver-coated glass mirror with a length of 3660mm, a width of 2440mm, and a thickness of 3mm, the process is as follows: glass cleaning→sensitization→supersensitization→silver plating→passivation→secondary passivation→priming→ Primer baking→finish paint→air cooling→pickling surface→display cleaning→finished product; its characteristic is that the silver plating process is divided into primary silver plating and secondary silver plating, and the primary silver plating process is performed first, followed by secondary silver plating process, wherein the temperature of the first silver plating is 23°C, and the silver plating time is 1 minute, so that the sil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a silver plating method for a glass mirror. The method comprises the steps of: cleaning the glass, sensitizing, super sensitizing, sliver plating, passivating, secondarily passivating, primer painting, primer baking, finish-paint painting, air cooling, surface scouring, indicating cleaning and acquiring finished product, wherein the silver plating process includes a primary silver plating and a secondary silver plating; the primary silver plating is performed before the secondary silver plating; the unit area silver mass on the glass is 100 to 200 mg / m2 after the primary silver plating; the reducing solution in the reaction solution is low speed reaction reducing solution; the unit area silver mass on the glass is 700 to 800 mg / m2 after the secondary silver plating; and the reducing solution in the reaction solution is high speed reaction reducing solution. The invention has the advantages of promoting the reflection ratio of the glass mirror and increasing the thickness.

Description

1. Technical field [0001] The invention relates to a silver plating method, in particular to a silver plating method for glass mirrors. 2. Background technology [0002] At present, the silver plating method of glass mirrors is as follows: glass cleaning → sensitization → hypersensitization → silver plating → passivation → secondary passivation → primer coating → primer baking → surface coating → air cooling → pickling Surface → display cleaning → finished product; the silver plating process adopts the method of one-time silver plating, that is, the reduction reaction of silver nitrate is carried out with the reducing solution, and the reaction temperature is 28-30°C; currently, the silver plating layer of the glass mirror is required to be made The reflectivity of the glass mirror is high and the thickness of the silver layer is increased at the same time; but to improve the reflectivity of the glass mirror, the compactness of the silver layer will be improved, which can on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/06
Inventor 陈俊律耿文龙陈泱光
Owner 江阴市京澄玻璃有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products