Method for preparing baking-free brick from yellow phosphorus slag and modified phosphogypsum

A technology of phosphogypsum and yellow phosphorus slag, which is applied in the field of unburned bricks, can solve the problems of unfavorable industrial production, high cost, and long brick curing time, and achieve the effects of high utilization rate, good quality, and shortened production cycle

Inactive Publication Date: 2012-10-31
KUNMING UNIV OF SCI & TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this method is that the cost of using high-alumina cement and alumina stone powder as the binder is relatively high, and secondly, the curing time of the adobe is long, which is not conducive to industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing baking-free brick from yellow phosphorus slag and modified phosphogypsum
  • Method for preparing baking-free brick from yellow phosphorus slag and modified phosphogypsum
  • Method for preparing baking-free brick from yellow phosphorus slag and modified phosphogypsum

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Crush 75% of yellow phosphorus slag, 25% of modified phosphogypsum, and 8% of sand (percentage by weight) until the particle size is less than 3mm, then add 5% of cement, add 7% of water for mixing, high pressure molding, demoulding, 60-80 ℃ steam curing, and finally the performance test of the product. Among them, the steam curing time is about 6 to 8 hours.

[0046] The measured product performance is as follows:

[0047] Compressive strength 10.6Mpa;

[0048] Flexural strength 2.7Mpa;

[0049] Meet the requirements of the standard "JC422-1991 (1996) non-fired ordinary bricks".

Embodiment 2

[0051] After pulverizing 72% of yellow phosphorus slag, 28% of modified phosphogypsum, and 5% of sand (percentage by weight) to a particle size of less than 3mm, add 5% of cement and 8% of water to mix and stir. Other procedures are the same as in Example 1.

[0052] The measured product performance is as follows:

[0053] Compressive strength 10.8Mpa;

[0054] Flexural strength 2.3Mpa;

[0055] Meet the requirements of the standard "JC422-1991 (1996) non-fired ordinary bricks".

Embodiment 3

[0057] 68% of yellow phosphorus slag, 32% of modified phosphogypsum, and 10% of sand (percentage by weight) were pulverized to a particle size of less than 3mm, then mixed with 3% of cement and 10% of water for mixing. Other procedures were the same as in Example 1.

[0058] The measured product performance is as follows:

[0059] Compressive strength 10.2Mpa;

[0060] Flexural strength 2.3Mpa;

[0061] Meet the requirements of the standard "JC422-1991 (1996) non-fired ordinary bricks".

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a baking-free brick prepared by using yellow phosphorus slag and modified phosphogypsum as raw materials and a preparation method thereof. The industrial waste yellow phosphorus slag and the modified phosphogypsum are used as basic raw materials, sand and cement are added into the raw materials, and the mixture in a weight ratio is prepared into a finished product by processes of crushing, proportioning, mixing, stirring, high-pressure shaping, stripping, steam curing and the like. A large amount of yellow phosphorus slag discharged by the yellow phosphorus industry anda large amount of phosphogypsum discharged by the phosphoric acid industry are comprehensively utilized, and meanwhile, various environmental pollutions caused by long-term stacking of the yellow phosphorus slag and the phosphogypsum are reduced. The baking-free brick prepared from the yellow phosphorus slag and the phosphogypsum has the advantages of high utilization rate of industrial waste slag, high consumption, simple production process, short production period, low cost, environmental protection and energy conservation; and the brick meets the national standard requirements for baking-free common bricks, and is a novel environment-friendly building material. The steam curing is performed on the formed brick blank so as to shorten the curing time, improve the compressive flexural performance of the brick and facilitate large-batch production.

Description

technical field [0001] The invention relates to a method for preparing non-fired bricks by using yellow phosphorus slag and modified phosphogypsum as raw materials. Background technique [0002] The land area of ​​our country is decreasing year by year, and the land resources are becoming more and more scarce. Since the production of clay bricks will consume a large amount of non-renewable land resources, it is no longer in line with the industrial policy. Therefore, my country banned the production of clay solid bricks in 2000. Various bricks for building materials that use fly ash, carbide slag, foundry steel slag, sandstone, etc. as alternative raw materials have emerged as the times require. [0003] Phosphogypsum is a by-product produced in the wet-process phosphoric acid production process, the main component is CaSO 4 2H 2 O, in addition to a small amount of F, P 2 o 5 、Al 2 o 3 , Fe 2 o 3 and organic matter etc. Phosphogypsum is mainly used in the preparatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00
Inventor 杨月红刘梦雪付廷栋舒敦涛李迎徐德才张小坤
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com