Catalyst for use in preparation of paraphenyldimethylamine and preparation method thereof

A technology of m-xylylenediamine and a catalyst is applied in the field of nickel catalyst, which can solve the problems of large catalyst loss, high production cost and high manufacturing cost, and achieves the effects of strong catalyst activity, low nickel content and environmental friendliness

Inactive Publication Date: 2011-04-27
NANJING UNIV +2
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003]At present, m-xylylenediamine is produced by the catalytic hydrogenation process of isophthalonitrile, and the catalysts used are common Raney nickel and modified Raney nickel Or amorphous nickel, etc., the nickel content of these catalysts reaches more than 60%, and the manufacturing cost is high
[0004]The existing catalysts have good initial activity, but poor stability. After being used in the reactor for a period of time, the hydrogenation activity of the catalyst decreases significantly. The possible reasons are: ① The existence of a small amount of impurities in isophthalonitrile may lead to partial deactivation of t...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] At 500°C in an air atmosphere, calcining pellets with a diameter of 1-2 mm prepared from pseudo-boehmite for 4 hours to obtain the corresponding alumina carrier. Detected as γ-Al 2 o 3 type with a specific surface area of ​​191 m 2 / g, the pore volume is 0.40 cm 3 / g, the pore size is 6.0 nm.

Embodiment 2

[0023] Add 6.2 g of nickel nitrate hexahydrate to 25 ml of distilled water to make a solution, and impregnate it on the alumina support prepared in Example 1, so that the content of metallic nickel in the catalyst is 5 wt%. The support impregnated with nickel components was dried at 100 °C for 10 h. The dried catalyst was calcined at 400 °C for 4 h in an air atmosphere to obtain a catalyst precursor. The catalyst precursor was reductively activated in pure hydrogen at 400 °C for 5 h to obtain the target catalyst in a reduced state.

[0024] Take 5.0g of the above catalyst, use the mixture of methanol and toluene (the volume ratio of the two = 1:4) as the solvent, the concentration of m-dicyanonitrile is 5.0%, the volume of the reaction solution is 125 ml, and put it into the reaction kettle, the reaction pressure = 6.0M Pa, reaction temperature=70 DEG C, after reaction time=1.5 h, sample chromatographic analysis showed that the conversion rate of m-dicyanonitrile was 62.4%, a...

Embodiment 3

[0026] 31.0 g of nickel nitrate hexahydrate was added to 25 ml of distilled water to form a solution, which was impregnated onto the alumina carrier prepared in Example 1, so that the content of metallic nickel in the catalyst was 25 wt%. The support impregnated with nickel components was dried at 100 °C for 24 h. The dried catalyst was calcined at 400 °C for 4 h in an air atmosphere to obtain a catalyst precursor. The catalyst precursor was reductively activated in pure hydrogen at 400 °C for 4 h to obtain the target catalyst in the reduced state.

[0027] Take 5 g of the above catalyst, use the mixture of methanol and toluene (the volume ratio of the two = 1:4) as the solvent, the concentration of m-dicyanonitrile is 7.5%, and the volume of the reaction liquid is 125 ml, and put it into the reaction kettle, the reaction pressure = 6.0M Pa, reaction temperature=70 ℃, after reaction time=1 h, sample chromatographic analysis showed that the conversion rate of m-dicyanonitrile ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Pore volumeaaaaaaaaaa
Apertureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a catalyst for use in the preparation of paraphenyldimethylamine, which is a supported nickel catalyst. The carrier of the catalyst is gamma-Al2O3 type aluminum oxide, the specific surface area of the carrier is 170 to 200m<2>/g, the pore volume is 0.35 to 0.45cm<3>/g, and the aperture is 4.5 to 6.0nm, the carrier is loaded with nickel and an auxiliary catalyst which may be copper, cobalt, iron or zinc or one or two of copper, cobalt, iron or zinc, the loaded nickel accounts for 5 to 25 percent of the total mass of the catalyst, the auxiliary catalyst accounts for 3 to8 percent of the total mass, and the carrier aluminum oxide accounts for the balance. When the catalyst disclosed by the invention is used, paraphenyldimethylamine can be prepared by hydrogenation ofisophthalodinitrile under milder conditions, the conversion rate of isophthalonitrile is 100 percent, and the selectivity of the paraphenyldimethylamine can reach 98.8 percent. The invention also discloses the preparation method of the catalyst.

Description

technical field [0001] The invention relates to a nickel catalyst, in particular to a supported nickel catalyst, and also relates to the preparation of m-xylylenediamine. technical background [0002] m-xylylenediamine is not only an epoxy resin curing agent with excellent performance and wide application, but also an important fine chemical intermediate. Its main uses are: ① series epoxy resin curing agent; ② new engineering materials Additives; ③Rubber additives, pesticides, fiber finishing agents, rust inhibitors, chelating agents, lubricants, paper processing aids and electronic chemicals are high value-added fine chemicals with broad application prospects. [0003] At present, m-xylylenediamine is produced by the catalytic hydrogenation process of isophthalonitrile. The common catalysts used are Raney nickel, modified Raney nickel or amorphous nickel, etc. The metal nickel content of these catalysts reaches 60%. Above, the manufacturing cost is high. [0004] The exis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J23/755B01J23/80C07C211/27C07C209/48
Inventor 季伟捷石天宝李慧秦怡生秦旭东蒋大智姚义刚贾涛
Owner NANJING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka