Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Method for preparing controllable ordered porous tin dioxide nano structures

A technology of tin dioxide and nanostructures, applied in the direction of tin oxide, etc., can solve the problems of difficult controllable and orderly porous tin dioxide nanostructures, harsh preparation and operating conditions, and limitations in the application of tin dioxide, and achieve high morphology Orderly, effective control of three-dimensional depth, and effective control of hole wall thickness

Inactive Publication Date: 2011-08-17
YANGZHOU UNIV
View PDF2 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The porous tin dioxide nanostructure produced by the sputtering method is similar to the anodic oxidation method, and its preparation and operating conditions are more harsh, which is difficult to apply to large-scale production
Although the sol method can prepare multilayer porous tin dioxide nanostructures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing controllable ordered porous tin dioxide nano structures
  • Method for preparing controllable ordered porous tin dioxide nano structures
  • Method for preparing controllable ordered porous tin dioxide nano structures

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The medicaments or reagents involved in the present invention are all analytically pure.

[0021] 8.75g of SnCl 4 4H 2 O was added to 100ml of absolute ethanol solution, heated to 80°C by a magnetic stirrer, kept at a constant temperature of 80°C in a water bath for 10h, and the rotor speed was 500r / min. Then it was cooled to room temperature and left to stand for 24 hours for aging treatment to obtain a tin dioxide sol solution.

[0022] Add 0.9g of styrene to 70ml of deionized water, heat to 70°C with a magnetic stirrer and water bath, and rotate at 500r / min, and set this solution as A solution. 0.115g of K 2 S 2 o 8 Add it into 5ml deionized water and sonicate for 20-30min, and set this solution as B solution. After keeping solution A at 70°C for 20 minutes, slowly drop into solution B under the action of a magnetic stirrer at a speed of 300 r / min. After the dropwise addition, keep at 70°C for 24 hours to obtain polystyrene pellets. The prepared polystyrene b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing controllable ordered porous tin dioxide nano structures, and belongs to the technical fields of gas sensitive sensing materials and solar cell preparation. The method comprises the following steps of: mixing SnCl4.4H2O and absolute ethanol in a certain ratio, keeping the mixture for 8 to 12 hours at the constant temperature of between 70 and 90 DEG C to obtain tin dioxide sol solution, and dripping the tin dioxide sol solution onto a substrate, the surface of which polystyrene spheres are deposited on; and drying, and performing high-temperature annealing to obtain the controllable ordered porous tin dioxide nano structures. By the method, the contact area of the materials and the external environment is greatly improved, and controllable adjustment of aperture size, pore wall thickness and three-dimensional depth of the product can be realized; and the product has excellent gas sensitive performance and photoelectric performance.

Description

technical field [0001] The invention discloses a method for preparing a controllable and ordered porous tin dioxide nanostructure. The key of the method is to prepare the controllable porous and ordered tin dioxide nanostructure by using an inverse opal structure, which belongs to gas-sensitive sensing materials and solar energy The field of battery manufacturing technology. Background technique [0002] SnO nanostructures have important applications in transparent conductive electrodes, solar cells, and especially gas sensors. As a gas-sensing sensing material, it first requires a relatively high gas sensitivity and a relatively large specific surface area, and secondly requires low power consumption, good chemical stability, corrosion resistance, and no pollution. Porous tin dioxide nanostructures are widely favored because of their larger specific surface area and better contact with external gases. However, at present, there are few preparation techniques for porous ti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01G19/02
Inventor 陈海涛周旭明杨文露陈小兵朱骏
Owner YANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com