Method for preparing anti-dripping polyester fibers

A polyester fiber, anti-melting dripping technology, applied in the direction of chemical post-treatment of single-component polyester rayon filament and synthetic polymer rayon filament, can solve the problems of restricted use, secondary hazards, melt dripping, etc. Achieve effective anti-droplet, high technical added value, significant economic and social benefits

Inactive Publication Date: 2013-01-02
WUHAN TEXTILE UNIV +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because polyester fiber is heated, melted, decomposed, burned, and has the phenomenon of melting and dripping, it is easy to cause secondary hazards and greatly restricts its use. The research significance of polyester fiber is very important

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A preparation method of anti-dripping polyester fiber, it comprises the following steps:

[0017] 1) Mixing: drying the polyester chips in a vacuum drying oven at 120° C. for 5 hours so that the water content in the polyester chips is lower than 0.02 wt%, and then adding them into a high-speed mixer;

[0018] Select trimethylolpropane trimethacrylate for use, join in the polyester chip according to 1% of the polyester chip quality (that is, the quality of trimethylolpropane trimethacrylate is 1% of the polyester chip quality), In a high-speed mixer, the crosslinking agent trimethylolpropane trimethacrylate and polyester chips are fully mixed to obtain a blend;

[0019] 2) Blending and extrusion: adding the blended material to a twin-screw extruder for blending and granulation to obtain particles (that is, cut into anti-dripping polyester chips);

[0020] 3) Melt spinning: drying the particles obtained by blending and granulation in a vacuum drying oven at 120° C. for 5...

Embodiment 6

[0025] A preparation method of anti-dripping polyester fiber, it comprises the following steps:

[0026] 1) Mixing: drying the polyester chips in a vacuum drying oven at 90°C for 4 hours so that the water content in the polyester chips is lower than 0.02 wt%, and then adding them to a high-speed mixer;

[0027] Select trimethylolpropane trimethacrylate for use, join in the polyester chip according to 5% of polyester chip quality (the quality that is trimethylolpropane trimethacrylate is 5% of polyester chip quality), In a high-speed mixer, the crosslinking agent trimethylolpropane trimethacrylate and polyester chips are fully mixed to obtain a blend;

[0028] 2) Blending and extrusion: adding the blended material to a twin-screw extruder for blending and granulation to obtain particles (that is, cut into anti-dripping polyester chips);

[0029] 3) Melt spinning: drying the particles obtained by blending and granulation in a vacuum drying oven at 90° C. for 4 hours, so that th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing anti-dripping polyester fibers. The method is characterized by comprising the following steps: 1) mixing materials: drying polyester chips, putting the dried polyester chips into an agitator, adding a crosslinking agent with mass being 0.5-5% that of the polyester chips and mixing in the agitator to obtain a co-mixture; 2) carrying out blending extrusion: adding the co-mixture to a twin-screw extruder for blending granulation to obtain granules; 3) melt spinning: drying the granules and then carrying out melt spinning by the existing melt spinning method of the polyester fibers to obtain primary anti-dripping polyester fibers; and 4) directly processing the primary anti-dripping polyester fibers with a 1.0-5MeV electron accelerator under theconditions that the irradiation dose is 10-50kGy, the beam current of the electron accelerator is 3-15mA and the irradiation time is 3-8s to obtain the anti-dripping polyester fibers. The method has the following beneficial effects: the anti-dripping polyester fibers are free of melting and dripping when burnt, can effectively resist dripping and can not release toxic gases or smoke; and the method is simple and practical.

Description

technical field [0001] The invention belongs to the technical field of chemical fiber materials, in particular to a preparation method of anti-droplet polyester fiber. Background technique [0002] Polyester fiber has the advantages of high modulus, high strength, high elasticity, good shape retention and heat resistance, and has become the most widely used and most consumed fiber variety. However, because polyester fiber is heated, melted, decomposed, burned, and has the phenomenon of melting and dripping, it is easy to cause secondary hazards and greatly restricts its use. The research on polyester fiber is of great significance. Contents of the invention [0003] The object of the present invention is to provide a method for preparing anti-melt-dripping polyester fibers, and the polyester fibers prepared by the method have the characteristics of anti-melt-dripping. [0004] In order to achieve the above object, the technical solution adopted by the present invention i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F11/08
Inventor 黄年华王晓广吴海燕王霞陈志军刘望清张翔苗馨匀
Owner WUHAN TEXTILE UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap