Heavy cotton viscose blended dual-elasticity yarn drill fabric and finishing process thereof

A double-elastic yarn card and fabric technology, applied in the textile field, can solve problems such as lack of elasticity and inability to make heavy fabrics, and achieve the effects of good pilling resistance, smooth hand feeling, drape texture, plump elastic recovery performance

Active Publication Date: 2011-09-14
YIXING XINLEQI TEXTILE PRINTING & DYEING
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Chinese patent application 2009102336092 discloses a "production process of cotton-bonded glossy silk fabric", which is cotton yarn and glossy silk dyed, warped, sizing, weaving, gray cloth repair, singeing, desizing, mercerizing, setting, It is made by pre-shrinking, and the control of various parameters in the process focuses on solving the problem of consistent tension between cotton and glossy yarn during weaving, and solving the problem of bubbles caused by tension differences in the finishing process, but this kind of fabric has no elasticity
Although this kind of fabric has elasticity, its weight is relatively light, and it is made of knitting. It is only suitable for underwear fabrics, and cannot be used as heavy fabrics for autumn and winter tops and bottoms.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Example 1, a thick cotton-viscose blended double-elastic yarn card fabric, which is a woven 2 / 1 right-hand oblique yarn card, 40 / 2 cotton viscose 70D spandex core-spun yarn in the warp direction, and 40 / 2 cotton viscose 70D spandex wrap in the weft direction Core yarn, the weight percentage of raw material composition is 57% cotton / 38% viscose / 5% spandex.

[0022] The finishing process is:

[0023] 1) Cotton fiber and viscose fiber are spun into 40s combed cotton-viscose blended yarn by ring spinning according to the weight ratio, and then 40s double-ply core-spun yarn is made from 70D spandex, which is woven into gray cloth. The gray cloth specification is The yarn count of the gray cloth is 40 / 2+70Dx40 / 2+70D, the density of the gray cloth is 74x48 threads / inch, the width of the gray cloth is 84 In., and the casting rate is 1.28;

[0024] 2) Tight desizing;

[0025] 3) Singeing cold stacking: After the desized cloth is singed and then padded, the cold stacking liquid...

Embodiment 2

[0037] Example 2, a thick cotton-viscose blended double-elastic yarn card fabric, which is a woven 2 / 1 right bias yarn card, 40 / 2 cotton viscose 70D spandex core-spun yarn in the warp direction, and a weft direction 40 / 2 cotton viscose 70D spandex bag Core yarn, the weight percentage of raw material composition is 55% cotton / 41% viscose / 4% spandex.

[0038] The finishing method refers to Example 1.

Embodiment 3

[0039] Example 3, a thick cotton-viscose blended double-elastic yarn card fabric, which is a woven 2 / 1 right-hand oblique yarn card, 40 / 2 cotton viscose 70D spandex core-spun yarn in the warp direction, and a weft direction 40 / 2 cotton viscose 70D spandex bag Core yarn, the weight percentage of raw material composition is 52% cotton / 42% viscose / 6% spandex.

[0040] The finishing method refers to Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a heavy cotton viscose blended dual-elasticity yarn drill fabric, and belongs to the technical field of textiles. The fabric containing 52 to 60 weight percent of cotton, 35 to 42 weight percent of viscose and 4 to 6 weight percent of polyurethane consist of woven 2 / 1 right oblique yarn drill, warp 40 / 2 cotton viscose 70D polyurethane covering yarns and weft 40 / 2 cotton viscose 70D polyurethane covering yarns serving as raw materials. The printing and dyeing processing problems caused by the property of the viscose and dual elasticity of warps and wefts are solved; the properties of cotton, viscose and polyurethane fibers are optimized and combined; and the fabric is flat and bright, uniform luster, slip handfeel, overhanging texture, good fluffing and pilling resistance, plump elasticity and good restoring elasticity, and is comfortable and fashionable to wear.

Description

technical field [0001] The invention relates to a heavy cotton-viscose blended double-elastic gauze fabric and a finishing process thereof, belonging to the technical field of textiles. Background technique [0002] The characteristics of viscose fiber have many advantages compared with cotton fiber: high hygroscopicity, soft and skin-friendly, not easy to generate static electricity, smooth and cool with drape skinny feeling, colorful dyeing, etc. It can be used with other fibers to obtain a unique fabric style. increasingly popular with consumers. [0003] Chinese patent application 2009102336092 discloses a "production process of cotton-bonded glossy silk fabric", which is cotton yarn and glossy silk dyed, warped, sizing, weaving, gray cloth repair, singeing, desizing, mercerizing, setting, It is pre-shrunk, and the control of various parameters in the process focuses on solving the problem of consistent tension between cotton and bright yarn during weaving, and solving ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D02G3/04D02G3/32D06B3/00D06B21/00D03D15/217D03D15/225D03D15/283D03D15/47D03D15/56
Inventor 甄峤源潘文英徐小峰
Owner YIXING XINLEQI TEXTILE PRINTING & DYEING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com