Method for flexible bonding of amorphous alloy steel sheet and special bonding compound

A technology of amorphous alloy and alloy steel, applied in the direction of binder type, non-polymer binder additive, benzofuran-indene copolymer binder, etc., can solve the problem of affecting the performance of amorphous core and amorphous transformer And other problems, to achieve the effect of improving the processing efficiency and performance level, low noise, and remarkable effect

Inactive Publication Date: 2013-07-17
SHANGHAI SUPERCONDUCTOR ENERGY EQUIP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Obviously, the traditional method of bonding with epoxy resin can be bonded, but it is very difficult to reopen after curing. Therefore, in the conventional method of bonding with epoxy resin, the opening of the amorphous core has to be bonded. , which affects the performance of amorphous core and amorphous transformer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for flexible bonding of amorphous alloy steel sheet and special bonding compound
  • Method for flexible bonding of amorphous alloy steel sheet and special bonding compound
  • Method for flexible bonding of amorphous alloy steel sheet and special bonding compound

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] formula:

[0038] 100 parts of liquid polysulfide rubber

[0039] Coumarone resin 20 parts

[0040] 35 parts of asbestos powder

[0041] 0.3 parts of dibutyl phthalate

[0042] Filament glass fiber 7 parts

[0043] Accelerator TT 0.6 parts

[0044] Zinc oxide 2 parts

[0045] Among them: the liquid polysulfide rubber adopts the domestic brand JLY-124.

[0046] Preparation method: Stir and mix the various components to obtain the product.

Embodiment 2

[0048] formula:

[0049] 100 parts of liquid polysulfide rubber

[0050] Coumarone resin 28 parts

[0051] 45 parts of asbestos powder

[0052] Dibutyl phthalate 0.1 parts

[0053] Filament fiberglass 3 parts

[0054] Accelerator TT 0.3 parts

[0055] Zinc oxide 1 part

[0056] Liquid polysulfide rubber adopts foreign brand LP-3 LP-2 LP-23.

[0057] Preparation method: Stir and mix the various components to obtain the product.

Embodiment 3

[0059] 100 parts of liquid polysulfide rubber

[0060] Coumarone resin 24 parts

[0061] 40 parts of asbestos powder

[0062] Dibutyl phthalate 0.2 parts

[0063] Filament glass fiber 5 parts

[0064] Accelerator TT 0.45 parts

[0065] Zinc oxide 1.5 parts

[0066] The liquid polysulfide rubber adopts the domestic brand JLY-124.

[0067] Preparation method: Stir and mix the various components to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for flexible bonding of an amorphous alloy steel sheet and a special bonding compound. The special bonding compound comprises the following components by weight: 100 parts of liquid polysulfide rubber, 20 to 28 parts of a coumarone-indene resin, 35 to 45 parts of asbestos powder, 0.1 to 0.3 parts of dibutyl phthalate, 3 to 7 parts of filament glass fiber, 0.3 to 0.6 parts of a promoter TT, and 1 to 2 parts of zinc oxide. According to the method for the flexible bonding of the amorphous alloy steel sheet and the special bonding compound provided in the invention, the processing efficiency and the performance level of an amorphous alloy iron core can be effectively improved with substantial effects; meanwhile, an amorphous transformer product, which is more energy efficient and has low noise, can be produced.

Description

technical field [0001] The invention relates to a method for flexibly bonding amorphous alloy steel sheets and a special bonding glue, belonging to the field of design and manufacture of power transformers. Background technique [0002] The application of amorphous alloy core as a magnetic circuit in the production of amorphous alloy transformer can make the amorphous transformer obtain very excellent low loss characteristics. In the manufacture of amorphous alloy transformers, the low loss level of amorphous alloy core represents the level of energy saving and consumption reduction of amorphous transformers. Therefore, the low loss characteristics of magnetic conduction of amorphous cores are very important for obtaining high-quality amorphous transformers. [0003] The amorphous core is cut and assembled from amorphous alloy steel strips. The quality of the cutting process and assembly process determines the performance of the amorphous core. In the assembly process, the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J181/04C09J145/02C09J11/04C09J11/06H01F41/02H01F27/26
Inventor 胡雄文
Owner SHANGHAI SUPERCONDUCTOR ENERGY EQUIP