Bamboo-wood mixed reconstituted timber and its processing method

A processing method and technology of recombined wood, applied to wood processing appliances, other household appliances, household components, etc., can solve the problems of low strength, poor forming texture, and difficult manufacturing, and achieve the effect of high strength and rich texture

Active Publication Date: 2011-11-30
ZHEJIANG TIANZHEN BAMBOO & WOOD DEV
View PDF13 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved and the technical task proposed by the present invention are to overcome the technical defects of poor forming texture, uneven material mixing, poor consistency, low strength, difficult manufacturing and high energy consumption existing in the existing single-material pressed slab, and provide a Bamboo-wood mixed recombined wood with rich texture after forming, uniform and dense material mixing, high strength, and convenient manufacture and processing method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo-wood mixed reconstituted timber and its processing method
  • Bamboo-wood mixed reconstituted timber and its processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention will be further described below in conjunction with the accompanying drawings and specific embodiments.

[0024] like figure 1 As shown, the bamboo-wood mixed recombined wood 1 includes bamboo 2 and wood 3, and the bamboo 2 and wood 3 are equal in length and in the same direction. Silk, the wood 3 is wood bundles and / or single wood chips, and the bamboo 2 and wood 3 are randomly filled with plant accessories such as walnut shells 4 and bamboo powder 5 .

[0025] Embodiment 1 of the processing method of bamboo and wood mixed heavy wood comprises the following steps carried out in sequence:

[0026] a. Bamboo 2 and wood 3 are heated and dried, and the moisture content is controlled at 10%. The bamboo is bamboo bundle monomer and / or conjoined bamboo filaments, and the wood is wood bundle and / or single wood chip;

[0027] b. Soak the dried bamboo and wood in the natural color or the water-soluble phenolic resin glue solution treated by toning for 6 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a restructured slab in building boards, in particular to a bamboo-wood mixed restructured lumber and a processing method thereof. Aiming at the technical defects of poor forming texture, uneven material mixing, poor consistency, low strength, difficult manufacturing and high energy consumption existing in the existing single-material pressed slab, the present invention provides a slab with rich texture after forming, uniform and compact material mixing. , high-strength, easy-to-manufacture bamboo-wood mixed recombined wood and its processing method, the bamboo-wood mixed rewood includes bamboo and wood, characterized in that the bamboo and wood are equal in length and in the same direction and are randomly stacked and pressed together. Synthetic profiles. The present invention presses profiles by mixing bamboo and wood. Wood is used to control texture patterns, and bamboo is used to fill holes and reduce gaps. The texture formed by the mixture of the two materials is richer, which is more beautiful than the existing single-material pressed slab, and finally pressed into shape The recombined wood is uniform and dense, with high strength; the two materials are filled and mixed with each other, and the amount of glue required is less than that of single material profiles.

Description

technical field [0001] The invention relates to a restructured slab in building boards, in particular to a bamboo-wood mixed restructured lumber and a processing method thereof. Background technique [0002] Existing common recombined timbers are multi-layer laminated composites of the same material or sheets, strips, silks or bundles of similar shapes of the same material are extruded and bonded after sizing, such as recombined bamboo boards hot-pressed with bamboo silk sizing, Technological wood made of pressed poplar or eucalyptus chips, and small-diameter wood recombined wood made of single branches, all of which have certain defects. Wood, a technical wood made of equal-length materials, due to the poor fluidity of the wood chips during pressing, the gap between the rolls is large, and glue is needed to fill the gaps and holes. The amount of glue used is not environmentally friendly, and the formed slabs obtained by pressing are consistent. Poor performance and low str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/12
Inventor 方庆华王益冰
Owner ZHEJIANG TIANZHEN BAMBOO & WOOD DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap