Hydrolysis-resistance alcoholysis-resistance glass fiber reinforced PPA (phenyl-propanolamine) material and preparation method thereof
A technology that is resistant to alcoholysis and hydrolysis, applied in the field of polymer materials, can solve the problems of failing to meet customer requirements, easy to be corroded, and reduce mechanical properties, and achieve high mechanical properties, excellent hydrolysis resistance, and simple preparation process. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0044] Example 1:
[0045] The weight percentage of PPA is 76.8% (the following are weight percentages), heat stabilizer H1610.4%, alcoholysis resistant protective agent 0.3%, hydrolysis resistant protective agent 0.2%, OP wax 0.6%, nucleating agent 0.2%, Weigh the black mother N541.5%, pour it into a blender and stir evenly. The mixed materials are added to the hopper of the twin-screw extruder, and the glass fiber HP361020% is added to the extruder through the side feed, and the composite material is extruded and granulated after melt blending. Among them, the temperature settings of each heating zone of the screw are as follows: temperature in zone one is 270℃; temperature in zone two is 290℃; temperature in zone three is 310℃; temperature in zone four is 300℃; head: 310℃; residence time is 2~3min, pressure is 16MPa.
Example Embodiment
[0046] Example 2:
[0047] The weight percentage of PPA is 61.8% (the following are weight percentages), heat stabilizer H1610.4%, alcoholysis resistant protective agent 0.3%, hydrolysis resistant protective agent 0.2%, OP wax 0.6%, nucleating agent 0.2%, Weigh the black mother N541.5%, pour it into a blender and stir evenly. The mixed materials are added to the hopper of the twin-screw extruder, and the glass fiber HP3610 35% is added to the extruder through the side feed, and the composite material is extruded and granulated after melt blending. Among them, the temperature settings of each heating zone of the screw are as follows: temperature in zone one is 270℃; temperature in zone two is 290℃; temperature in zone three is 310℃; temperature in zone four is 300℃; head: 310℃; residence time is 2~3min, pressure is 16MPa.
Example Embodiment
[0048] Example 3:
[0049] The weight percentage of PPA is 46.8% (the following are weight percentages), heat stabilizer H1610.4%, alcoholysis resistant protective agent 0.3%, hydrolysis resistant protective agent 0.2%, OP wax 0.6%, nucleating agent 0.2%, Weigh the black mother N541.5%, pour it into a blender and stir evenly. The mixed materials are added to the hopper of the twin-screw extruder, and the glass fiber HP361050% is added to the extruder through the side feed, and the composite material is extruded and granulated after melt blending. Among them, the temperature settings of each heating zone of the screw are as follows: temperature in zone one is 270℃; temperature in zone two is 290℃; temperature in zone three is 310℃; temperature in zone four is 300℃; head: 310℃; residence time is 2~3min, pressure is 16MPa.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap