Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Method for treating sintering granules

A processing method and granulation technology, which are applied in the field of processing granulated materials for sintering, can solve problems such as cohesion of fine particles, and achieve the effects of inhibiting re-dispersion and inhibiting strength reduction.

Inactive Publication Date: 2012-01-25
NIPPON STEEL & SUMITOMO METAL CORP
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, although Patent Document 3 has a description of adding bentonite to the raw material, adding water to granulate it, and using it effectively as an aggregate, it is considered that there is also a large amount of aggregation of fine particles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for treating sintering granules
  • Method for treating sintering granules
  • Method for treating sintering granules

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0106] Next, examples performed to confirm the effects of the present invention will be described.

[0107] First, the result of adhering the strength-decreasing inhibitor to the surface layer of the quasi-granulated material produced using the above-mentioned conventional granulation line will be described.

[0108] Using a combination of several types of iron ore powder and sintering raw materials such as carbon materials, lime, and serpentinite (ore powder: 70.5%, lime: 10.0%, serpentine: 1.0%, carbon material: 3.5%, Return ore: 15.0%, the total is 100%), using a drum mixer (granulator), mixing for 4 minutes while adding water to granulate, and adjusting the moisture content of the granulated material to 7% by mass. In this wet granulation, quicklime which functions as a clay-based binder is added. In addition, the moisture content of the granulated material is the ratio of the moisture to the sum of the dry weight and the moisture of the granulated material.

[0109] The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Disclosed is a method for treating sintering granules, which enables the maintenance of strength of granules even when the granules are exposed to excess moisture in a wet zone or when dry granules are mixed with wet granules and the dry granules reabsorb moisture, and which can achieve a continuous granulation treatment in a continuous treatment line. The method comprises supplying coated granules into a sintering machine, wherein the coated granules comprise: granule which are produced by subjecting a raw material containing an accessory raw material comprising a iron ore powder, a carbon material and caustic lime to a wet granulation procedure using a binder to produce granules; and at least one strength reduction-preventing agent selected from a coagulant, a hydrophobizing agent and a water repellent agent, which is adhered on the surfaces of the granules.

Description

technical field [0001] The present invention relates to a method for treating granulated materials for sintering used as raw materials for blast furnaces. Background technique [0002] Sintered ore, which is a raw material for a blast furnace, is obtained by adding water to iron ore, fuel, auxiliary raw materials, etc., using a granulator, mixing and granulating them, and firing them in a sintering machine. In order to maintain and improve the productivity of the sintered ore, it is important to ensure the air permeability in the sintered raw material being fired in the sintering machine, and granulation becomes an indispensable operation. [0003] However, the water used for granulation evaporates during the firing process, forming a so-called wet zone that condenses in the lower unfired granules (granules; granules), and the granules in this excess water The collapse of the material causes the problem of hindering the ventilation in the sintering machine. In addition, in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B1/16
CPCC22B1/244C22B1/2413C22B1/20C22B1/2406C22B1/16
Inventor 八代健一长田淳治
Owner NIPPON STEEL & SUMITOMO METAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com