Water montmorillonite nano composite heat insulating waterproof paint and preparation method thereof

A nano-composite, thermal insulation technology, applied in the direction of coating, can solve problems such as unsatisfactory, and achieve the effects of environmental protection, long service life, good thickening performance and thixotropy

Active Publication Date: 2012-02-22
CHINA MCC17 GRP
View PDF4 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the exterior wall coating prepared by the above-mentioned technology is still unsatisfactory in terms of waterproof, thermal insulation, environmental protection, outdoor weather resistance, adhesion and antibacterial self-cleaning function.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042]The total number of parts is based on 1000 parts, and the prepared water-based montmorillonite nanocomposite thermal insulation and waterproof coating includes the mass parts of the following components:

[0043] Nanocomposite Emulsion 350

[0044] Silicone acrylic emulsion 110

[0045] Rutile titanium dioxide 120

[0046] Organically modified nano-montmorillonite 120

[0047] Nano zinc oxide 20

[0048] Nano Titanium Oxide 20

[0049] Nano silica 10

[0050] Nano aluminum oxide 20

[0051] AMP-95 3.0

[0052] Coalescent 5.0

[0053] STXP-4 3.5

[0054] 5040 2.0

[0055] PE100 1.0

[0056] Ethylene Glycol 5.0

[0057] STFM-1 1.0

[0058] Water 209.5

[0059] The preparation method of the present embodiment is as follows:

[0060] At a stirring speed of 400r / min, firstly mix water, organically modified nano-montmorillonite, nano-oxide, rutile titanium dioxide, wetting agent, dispersant, and half of the defoaming agent. The stirring speed was adjusted to 500...

Embodiment 2

[0062] The total number of parts is based on 1000 parts, and the prepared water-based montmorillonite nanocomposite thermal insulation and waterproof coating includes the mass parts of the following components:

[0063] Nanocomposite Emulsion 310

[0064] Pure acrylic emulsion 110

[0065] Rutile titanium dioxide 100

[0066] Organically modified nano-montmorillonite 120

[0067] Nano zinc oxide 20

[0068] Nano Titanium Oxide 30

[0069] Nano silica 30

[0070] Nano aluminum oxide 20

[0071] AMP-95 3.5

[0072] Coalescent 6.0

[0073] STXP-4 4.0

[0074] 5040 2.5

[0075] PE100 1.5

[0076] Ethylene Glycol 5.5

[0077] STFM-1 0.6

[0078] Huake-981 0.6

[0079] Water 235.8

[0080] The preparation method of the present embodiment is as follows:

[0081] At a stirring speed of 500r / min, firstly mix water, organically modified nano-montmorillonite, nano-oxide, rutile titanium dioxide, wetting agent, dispersant, and half of the defoaming agent. The stirring spee...

Embodiment 3

[0083] The total number of parts is based on 1000 parts, and the prepared water-based montmorillonite nanocomposite thermal insulation and waterproof coating includes the mass parts of the following components:

[0084] Nanocomposite Emulsion 330

[0085] Vinyl Acrylic Lotion 60

[0086] Silicone acrylic emulsion 60

[0087] Rutile titanium dioxide 150

[0088] Organically modified nano-montmorillonite 100

[0089] Nano zinc oxide 30

[0090] Nano Titanium Oxide 10

[0091] Nano silica 10

[0092] Nano aluminum oxide 10

[0093] AMP-95 3.5

[0094] Coalescent 6.5

[0095] STXP-4 3.5

[0096] 5040 3.0

[0097] PE100 1.0

[0098] Glycol 6.5

[0099] Huake-981 1.0

[0100] water 215

[0101] The preparation method of the present embodiment is as follows:

[0102] At a stirring speed of 600r / min, firstly mix water, organically modified nano-montmorillonite, nano-oxide, rutile titanium dioxide, wetting agent, dispersant, and half of the defoaming agent. The stirring...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
solid contentaaaaaaaaaa
Login to View More

Abstract

The invention discloses water montmorillonite nano composite heat insulating waterproof paint and a preparation method thereof. The water montmorillonite nano composite heat insulating waterproof paint comprises the following ingredients in percentage by mass: 30 to 35 percent of nano composite emulsion, 10 to 15 percent of polymer emulsion, 10 to 15 percent of rutile-type titanium pigment, 10 to15 percent of organic modified nano montmorillonite, 5 to 10 percent of nano oxide, 0.3 to 0.35 percent of pH adjusting agent, 0.50 to 0.65 percent of film-forming additive, 0.35 to 0.4 percent of elastic foam killer, 0.20 to 0.30 percent of wetting agent, 0.10 to 0.15 percent of dispersion agent, 0.50 to 0.65 percent of anti-freezing agent, 0.10 to 0.15 percent of sterilization antiseptic and 20to 25 percent of water. The water montmorillonite nano composite heat insulating waterproof paint not only has good compatibility, dispersion performance and good stability, but also has good water resistance, heat insulation, environmental protection, outdoor weather resistance and good adhesive attraction and has an antibacterial self-cleaning function.

Description

technical field [0001] The invention relates to a thermal insulation and waterproof material for building exterior walls, in particular to a water-based nanocomposite thermal insulation and waterproof coating and a preparation method thereof, belonging to the production field of building energy-saving and environmental protection coatings. Background technique [0002] Since the 1970s, the world's climate has warmed, and the earth's energy has been increasingly depleted. Building energy consumption accounts for 30% to 40% of human energy consumption, and most of them are used for heating and air conditioning. It is of great practical significance to develop thermal insulation coatings, especially thermal insulation coatings for exterior walls of buildings that are closely related to human life. The waterproof quality of building exterior walls is also an important indicator for evaluating the quality of construction projects. Therefore, the development of waterproof and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D125/14C09D131/04C09D7/12C09D5/00
Inventor 张千峰尹万云陈兴顺陈均金仁才
Owner CHINA MCC17 GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products