Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Nano-antirust coating

An anti-rust coating and nano technology, applied in anti-corrosion coatings, coatings and other directions, to achieve the effects of good resilience, high tensile strength and superior elongation

Inactive Publication Date: 2012-03-14
NANTONG TONGZHOU DISTRICT JINCHEN PAINT FACTORY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the current coatings are used for outdoor equipment, so the temperature changes throughout the year, and the temperature cracks caused by thermal expansion and contraction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] A nano-antirust coating is prepared uniformly by high-speed dispersion and stirring with a mixer according to the following raw materials: 46 parts of nano-polyacrylate emulsion, 30 parts of nano-scale titanium dioxide, 20 parts of ethylene glycol, and 10 parts of sodium carboxymethyl cellulose , 5 parts of heavy calcium powder, 6 parts of binder, 10 parts of cellulose acetate, 35 parts of deionized water, 5 parts of tannic acid, 1 part of PH regulator, 2.5 parts of thickener.

[0009] The detection performance of this product is as follows:

[0010] water resistance

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a nano-antirust coating. The nano-antirust coating is mainly prepared by stirring the following raw materials, wherein the raw materials comprise, by weight, 46 parts of nano-polyacrylate emulsion, 30 parts of nano-scale titanium dioxide, 20 parts of ethylene glycol, 10 parts of sodium carboxymethyl cellulose, 5 parts of heavy calcium powder, 6 parts of a binder, 10 parts of cellulose acetate, 35 parts of deionized water, 5 parts of tannic acid, 1 part of a pH value adjusting agent and 2.5 parts of a thickening agent. The product of the present invention has excellent performances of excellent extensibility, good elasticity, high tensile strength, water preventing, oxygen preventing, corrosion protection, and the like.

Description

technical field [0001] The invention relates to a nano antirust paint. technical background [0002] Metal corrosion is the result of chemical or electrochemical reactions between the surface of the metal and the medium in the surrounding environment from the surface to the inside, causing the metal to be damaged and lose its original properties. People have studied various measures to prevent and inhibit the corrosion of metals, among which coating anti-rust is an effective method. Most of the current coatings are used for outdoor equipment, so the temperature changes throughout the year and the temperature cracks caused by thermal expansion and contraction. Contents of the invention [0003] The purpose of the invention is to provide a nanometer antirust coating in order to overcome the deficiencies of the prior art. [0004] In order to solve the above problems, the previous technical solution of the present invention is: a kind of nano-antirust coating is made by sti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D101/26C09D101/12C09D7/12C09D5/08
Inventor 薛美娟
Owner NANTONG TONGZHOU DISTRICT JINCHEN PAINT FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products