Corrosion-proof easily-demoulded nylon-66 plastic

An easy-release and corrosion-resistant technology, applied in the field of corrosion-resistant and easy-release nylon 66 plastics, can solve the problems of shortened plastic life, not easy to release, and enterprise capital problems, and achieves non-corrosion, good self-lubricating performance, Good wear resistance

Inactive Publication Date: 2012-03-21
SUZHOU IND PARK XINFENGLIN PLASTIC TECH
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the plastics provided on the market generally have the characteristics of low corrosion resistance and low mold release performance. Although some improvements have been made on the market, it is still not easy to release the mold during the manufacturing process, and there are still certain difficulties. In addition , the anti-corrosion effect of the plastic made is not obvious, and it will still corrode due to long-term use or contact with some acid-base items, so that the life of the plastic will also be shortened, and there will be great pollution to the environment after the plastic is discarded. The constant replacement of plastic will also cause certain financial problems for the enterprise

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] Embodiment 1 provides a kind of corrosion-resistant and easy-release nylon 66 plastic, which is composed of the following components in weight ratio, nylon 66: 68%, graphite powder: 18.5%; antioxidant: 2.1%; heat stabilizer: 2.5%; Joint agent: 1.9%; high molecular weight silicone oil: 2.1%; activated carbon: 4.9%.

[0010] The following is the specific working principle of this embodiment:

[0011] First, the mixture containing nylon 66, graphite powder, antioxidant, heat stabilizer, coupling agent, and high molecular weight silicone oil is heated to a temperature not lower than the melting point of polyester to prepare a Melt flow rate and 30-150% swollen nylon 66 synthetic resin, and then thermally foaming the nylon 66 synthetic resin with the help of a foaming agent to obtain a 50% nylon 66 saline solution Then use activated carbon to filter and remove impurities, and then saturate, and the saturated solution of nylon 66 should be dried in 70-80T hot air circulation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an organic polymer composite, in particular to corrosion-proof easily-demoulded nylon-66 plastic, which comprises, by weight, 66:65-85% of polyamide, 2-32% of powdered graphite, 0.3-2.7% of antioxidant, 0.5-3.2% of heat stabilizer, 0.4-2.9% of coupling agent, 0.1-3.2% of high-molecular-weight silicon oil and 0.5-5.5% of activated carbon. The corrosion-proof easily-demoulded nylon-66 plastic has the advantages that self-lubricating performance and corrosion-proof performance of graphite are excellent, automatic demoulding can be achieved during injection molding or extruding of finished products, demoulding agent is not needed, and prepared plastic is not easy to corrode due to the corrosion-proof graphite.

Description

technical field [0001] The invention relates to an organic polymer composite material, more specifically, relates to a corrosion-resistant and easy-release nylon 66 plastic. Background technique [0002] After long-term struggle and opening up to the world, China's plastics industry has formed a relatively complete industrial system and has become a basic material industry that keeps pace with steel, cement, and wood. As a new type of material, its application fields have far exceeded the above three. Since the entry of this material into the 21st century, China's plastics industry has made remarkable achievements and achieved a historic leap. As one of the pillar industries of the light industry, the plastics industry has maintained a growth rate of more than 10% in recent years. While maintaining a relatively fast development speed, the economic benefits have also improved. The total output value of enterprises above designated size in the plastic products industry ranks ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08K13/02C08K3/04B29C45/76B29C45/78
Inventor 王志凤
Owner SUZHOU IND PARK XINFENGLIN PLASTIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products