Non-petroleum base complete degradation master batch and preparation method thereof

A completely degradable, non-petroleum-based technology, applied in the field of non-petroleum-based degradable masterbatch and its preparation, masterbatch and its preparation, can solve the problem of small proportion, precipitation of small molecules, and inability to completely degrade the masterbatch and other issues to achieve the effect of saving production costs and protecting the environment

Active Publication Date: 2012-03-28
MALION NEW MATERIALS CO LTD
View PDF2 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The masterbatch formula system is too complicated, and there are many types of small molecule additives, which will affect the processing of fully degradable material products, easily cause small molecule precipitation and other problems, and there is a certain risk
CN102040814A provides a black masterbatch specially used for polylactic acid-based degradable plastics. The formula system also contains petroleum-based non-degradable additives such as polyethylene wax, ethylene-vinyl acetate wax and EBS, which cannot realize the real sense of color masterbatch. Completely degraded
[0004] Degradable materials have experienced the development from "degradable" to "full degradable". Partially degradable materials such as starch-filled polypropylene or polyethylene materials, only the starch part can be degraded, so the traditional color masterbatch with polyethylene as the carrier It can be used in this kind of degradable material products, but degradable materials have now developed to the stage of fully degradable materials, which requires that the coloring masterbatch of fully degradable material products should also have the performance of complete degradation. None of the several patents achieved the complete degradability of the composition of the masterbatch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Formula: (unit is KG)

[0032] Polybutylene succinate PBS: 30

[0033] Titanium dioxide: 70

[0034] The preparation method is as follows:

[0035] The materials of each component are transported to the hopper of the continuous mixer through the metering device according to the dosage of the formula. The feeding speed is 200kg / hr, and are driven by the double rotors into the mixing chamber for shearing, kneading and banburying into a melt shape. The speed of the refining machine is 200 rpm, the feeding screw channel section is 40°C, the forward screw structure section is 150°C, the push screw structure section is 170°C, the melt transfer section is 150°C, the front opening of the internal mixer is 10%, and the melt enters In the single-screw extruder, the speed of the single-screw extruder is 30 rpm, the temperature range is set at 130°C-140°C-150°C-150°C-160°C-155°C-150°C, and the material passes through a 200-mesh screen Afterwards, it is extruded through the die o...

Embodiment 2

[0038] Formula: (unit is KG)

[0039] Polybutylene succinate PBS: 30

[0040] Titanium dioxide: 60

[0041] Barium sulfate: 10

[0042] The preparation method is as follows:

[0043] The materials of each component are transported to the hopper of the continuous mixer through the metering device according to the dosage of the formula. The feeding speed is 300kg / hr. The speed of the refining machine is 250 rpm, the feeding screw channel section is 40°C, the forward screw structure section is 150°C, the push screw structure section is 170°C, and the melt transfer section is 160°C. The front opening of the internal mixer is 30%, and the melt enters In the single-screw extruder, the speed of the single-screw extruder is 35 rpm, the temperature range is set at 130°C-140°C-145°C-150°C-155°C-145°C-140°C, and the material passes through a 100-mesh screen Afterwards, it is extruded through the die opening, cut into pellets under water and transported into the dryer for drying and m...

Embodiment 3

[0046] Formula: (unit is KG)

[0047] Polyhydroxyalkanoate P3 / 4HB (4HB content: 15%): 40

[0048] Polybutylene succinate PBS: 10

[0049] Carbon black: 50

[0050] The preparation method is as follows:

[0051]Each component material is transported to the hopper of the continuous internal mixer through the metering device according to the dosage of the formula. The feeding speed is 1000kg / hr, and is driven by the double rotors into the internal mixing chamber for shearing, kneading, and internal mixing into a melt shape. The speed of the mill is 500 rpm, the feeding screw channel section is 60°C, the forward spiral structure section is 155°C, the push-back spiral structure section is 180°C, and the melt transfer section is 170°C. In the single-screw extruder, the speed of the single-screw extruder is 50 rpm, the temperature range is set at 130°C-140°C-150°C-160°C-170°C-160°C-150°C, and the material passes through a 100-mesh sieve After the screen is extruded through the di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The embodiment of the invention discloses a non-petroleum base complete degradation master batch which comprises the following components in percentage by weight: 30%-50% of carrier, 20%-70% of pigment and 0-60% of stuffing, wherein the carrier is a biological base complete degradation polymer; the biological base complete degradation polymer comprises one or two of hydroxy fatty acid ester PHA series, polylactic acid PLA and polydiethylene glycol sebacate PBS. The master batch prepared by the invention contains no petroleum base and no degradable addition agent; and the needed carrier is derived from renewable resources, thereby realizing the complete degradation in the true sense and more effectively promoting the application of a degradable material and the protection of environments.

Description

technical field [0001] The invention belongs to the field of chemical industry and relates to a color masterbatch and a preparation method thereof, in particular to a non-petroleum-based degradable color masterbatch and a preparation method thereof Background technique [0002] In the past nearly one hundred years, the polymer material industry has achieved rapid development. The application and development of synthetic polymer materials have greatly facilitated people's lives, but the extensive use of disposable non-degradable products has brought serious environmental pollution problems. The problem of "white pollution" has attracted global attention. Countries have invested manpower and financial resources in the research and development of fully biodegradable materials. After nearly two decades of development, the research and development of fully degradable materials has made great progress. Fully degradable materials Products are gradually accepted by people because o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04C08L67/02C08L3/02C08K3/22C08K3/04C08K3/26C08K3/34C08K3/30C08J3/22
Inventor 黄伟汕张朝凯陈贤裕佘维深
Owner MALION NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap