High-strength cold rolling transformation induced plasticity steel plate and preparation method thereof

Abstract

The invention provides a high-strength cold rolling transformation induced plasticity steel plate and a preparation method thereof. The high-strength cold rolling transformation induced plasticity steel plate comprises the following components by weight percentage: 0.1%-0.5% of C, 0.1%-0.6% of Si, 0.5%-2.5% of Mn, 0.02%-0.12% of P, less than or equal to 0.02% of S, 0.02%-0.5% of Al, less than or equal to 0.01% of N, 0.1%-1.0% of Cu and the rest Fe. The preparation method comprises the following steps of: (a) refining molten steel meeting a component condition, and casting into a blank; (b) rolling, wherein the heating temperature is 1,100-1,250 DEG C, the heat preservation time is 1-4h, the initial rolling temperature is 1,100 DEG C, the final rolling temperature is 750-900 DEG C, the coiling temperature is less than 700 DEG C, the thickness of a hot rolled steel plate is 2-4mm, and the cold rolling accumulated pressing amount is 40-80%; and (c) continuous annealing, wherein the annealing temperature is 700-Ac3+50 DEG C, the heat preservation time is 30-360s, the cooling speed is 10-150 DEG C/s, the aging temperature is 250-600 DEG C, the aging time is 30-1,200s, and the hot roller steel plate is cooled at the speed of 5-100DEG C/s to be at the room temperature. The steel plate disclosed by the invention has the bending strength of 380-1,000 MPa, tensile strength of 680-1,280 MPa and elongation of 15-30%.

Description

technical field [0001] The invention belongs to the technical field of iron and steel metallurgy products, and in particular relates to a high-strength cold-rolled phase-change-induced plastic steel plate and a preparation method thereof. Background technique [0002] As people's requirements for automobile safety, environmental protection, energy saving, and weight reduction continue to increase, the application of advanced high-strength steel in automobiles continues to increase. TRIP (Transformation Induced Plasticity) steel, as an important member of advanced high-strength steel, has attracted the general attention of major automobile manufacturers and steel companies because of its comprehensive properties such as high strength, high plasticity and high impact. [0003] Most traditional TRIP steels are designed with high Si composition, and its typical composition is 0.2%C-1.5%Si-1.5%Mn. This composition system has the characteristics of high strength, good plasticity a...

AI Technical Summary

Problems solved by technology

The disadvantage is that due to the high silicon content, the surface quality of the product is deteriorated, and it is difficult to coat and weld

Its disadvantages are: the high Al content leads to blockage of the nozzle in the continuous casting production process, making continuous production difficult. At the same time, due to the lack of solid solution strengthening of Al, the strength of TRIP steel is low

Its shortcoming is that no alloy elements that can strengthen