Metal powder type flux-cored wire and preparation and application thereof

A technology of flux-cored welding wire and metal powder core, which is applied in the field of low-alloy steel metal powder-cored flux-cored welding wire and its preparation field, can solve the problems of poor processability of metal powder-cored flux-cored welding wire, etc., and achieves good welding process adaptability, The effect of good weld formation and wide source

Inactive Publication Date: 2012-05-02
WUHAN TEMO WELDING CONSUMABLES CO LTD
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is the probl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal powder type flux-cored wire and preparation and application thereof
  • Metal powder type flux-cored wire and preparation and application thereof
  • Metal powder type flux-cored wire and preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The present invention will be further described below in conjunction with specific examples, so that those skilled in the art can better understand the present invention and implement it, but the given examples are not intended to limit the present invention.

[0032] The metal powder-cored flux-cored welding wire of the present invention includes a powder filled with a carbon steel sheath filled in the carbon steel sheath, wherein the medicine powder contains the following components and their percentages in the total weight of the welding wire are as follows:

[0033] TiO 2 0.20~1.5%;

[0034] SiO 2 0.1~0.5%;

[0035] Na 2 O or K 2 A kind of O or its arbitrary ratio mixture 0.1~0.50%;

[0036] Si 0.15~0.65%;

[0037] Mg 0.08~0.45%;

[0038] Mn 0.9~2.4%;

[0039] Cr 0.15~1.0%;

[0040] Ni 1.5~4.5%;

[0041] Ti 0.15~0.45%;

[0042] B 0.004~0.012%;

[0043] NaF or CaF 2 One or two or more arbitrary mixtures 0.5~1.5%;

[0044] Wherein, the c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a metal powder type flux-cored wire comprising a carbon steel skin and powders filled inside it. The powders comprise the following components and percent thereof accounting total weight of the flux-cored wire: TiO2 0.20 to 1.5%, SiO2 0.1-0.5%, any one of Na2O or K2O or mixture with optimal mixing ratio 0.1-0.50%, SiO 0.15-0.65%, Mg 0.08-0.45%, Mn 0.9-2.4%, Cr 0.15-1.0%, Ni 1.5-4.5%, Ti 0.15-0.45%, B 0.004-0.012% and any one of NaF or CaF2 or mixture with optimal mixing ratio 0.5-1.5%. When the flux-cored wire is being welded, slag quantity on the welding seam surface is small, the deposition efficiency is high, the sputtering is few, the flux-cored wire has good low temperature impact toughness and anticracking ability, and diffusible hydrogen reaches the super low hydrogen level.

Description

technical field [0001] The invention relates to a welding material for metal welding, specifically a carbon dioxide or argon-rich (80%Ar+20%CO 2 ) Low-alloy steel metal powder-cored flux-cored wire for gas shielding and its preparation. Background technique [0002] Flux-cored wire is a high-efficiency welding material, which has many advantages such as high welding efficiency, shortened welding cycle, good welding process performance, beautiful weld shape, and small welding deformation. Therefore, it is widely used in the welding of steel structures such as ships and bridges. [0003] At present, flux cored wires on the market mainly include titanium type, alkali type and titanium-alkaline type, while metal powder cored flux cored wires have been developed to a certain extent abroad, but domestic research on this type of flux cored wires is less , in the newly revised low-alloy steel flux-cored wire standard GB / T 17493-2008, the metal powder-cored flux-cored wire for low-al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/368B23K35/40B23K9/16
Inventor 李磊田海成刘玉双韩海峰张亚平
Owner WUHAN TEMO WELDING CONSUMABLES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap