Coating material capable of reducing light reflection of glass surface

A technology for coating materials and glass surfaces, applied in the direction of coatings, etc., can solve the problems of reducing the refractive index of the film layer and affecting the anti-aging performance of the film layer

Inactive Publication Date: 2012-06-06
常熟卓辉光电科技股份有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The researchers found that the porous sponge-like SiO 2 Anti-reflection film can effectively reduce the refractive index of the film layer, but the above SiO 2 The more porosity of the anti-reflection film affects the anti-aging performance of the film layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Mix tetraethyl orthosilicate, ethanol, water, nitric acid, and ammonia water at a molar ratio of 1:10:8:0.05:0.1, stir for 24 hours, add 12 grams of P123, 8 grams of Tritonx-100 and 6 grams of hexamethylene base imine, stirred for 24 hours, refluxed for 5 hours and left to stand for 72 hours to make a coating material.

[0013] The above materials are uniformly coated on the glass surface, dried in an oven at 100°C for 4 hours, and then heated to 400°C for 2 hours. The anti-reflection rate of the obtained film is 2.2%, and the strength and aging resistance of the film are good.

Embodiment 2

[0015] Mix tetraethyl orthosilicate, ethanol, water, nitric acid, and ammonia in a molar ratio of 1:40:8:0.05:0.1, stir for 24 hours, add 15 grams of P123, 18 grams of Tritonx-100 and 10 grams of hexamethylene base imine, stirred for 24 hours, refluxed for 5 hours and left to stand for 72 hours to prepare a coating solution.

[0016] The above materials are uniformly coated on the glass surface, dried in an oven at 100°C for 4 hours, and then heated to 400°C for 2 hours. The antireflection rate of the obtained film is 2.4%, and the strength and aging resistance of the film are good.

Embodiment 3

[0018] Mix tetraethyl orthosilicate, ethanol, water, nitric acid, and ammonia in a molar ratio of 1:32:8:0.05:0.1, stir for 24 hours, add 18 grams of P123, 10 grams of Tritonx-100 and 15 grams of hexamethylene base imine, stirred for 24 hours, refluxed for 5 hours and left to stand for 72 hours to prepare a coating solution.

[0019] The above materials are evenly coated on the glass surface, dried in an oven at 100°C for 4 hours, and then heated to 400°C for 2 hours. The anti-reflection rate of the obtained film is 2.8%, and the strength and anti-aging performance of the film are good.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a coating material capable of reducing light reflection of a glass surface. The coating material comprises the components of ethyl orthosilicate, ethanol, water, nitric acid and ammonia water and the auxiliary agents of ethyl orthosilicate, P123, Tritonx-100 and hexamethyleneimine. A film formed after the coating material provided in the invention is coated on a glass surface is composed of cylindrical protrusions which present a certain rule and are vertically arranged, and the top of each of the cylindrical protrusions is semispherical, which enables the refractive index of the glass surface to gradiently vary when only one layer of the film is coated on the glass surface, thereby enabling reflectivity of the glass surface to be reduced.

Description

technical field [0001] The invention relates to a coating material, in particular to a coating material for reducing light reflection on a glass surface. Background technique [0002] At present, widely used lamps and lanterns all use glass as the light-transmitting medium. The light transmittance of ordinary glass can only reach 92%, and the low light transmittance seriously affects the light transmission of the lamp. [0003] The refractive index of glass is about 1.5, reducing the light reflection of glass can improve the light transmittance of glass. When making lampshades in the glass production industry, the content of impurities in the glass is generally reduced as much as possible, especially the iron content in the glass, so as to reduce the absorption of light by the glass body, and reducing the impurities of the glass body will greatly increase the production cost and cost of the glass. manufacturing difficulty. [0004] The researchers found that the porous spo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D7/12C09D5/00C03C17/23
Inventor 苏晓燕苏怡杨耀武
Owner 常熟卓辉光电科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products