Blended yarn of jute fiber, polyester fiber and nylon fiber and application of blended yarn

A technology of nylon fiber and blended yarn, which is applied in fiber treatment, biochemical fiber treatment, yarn, etc., can solve the problems that restrict the application and development of jute fiber, jute fiber is thick and rigid, and achieve good spinnability and improved Good hardness, wrinkle resistance and shape retention

Inactive Publication Date: 2012-06-13
JIANGSU REDBUD DYEING TECH CO LTD
View PDF11 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the shortcomings of jute fiber such as thick fiber, short length, high rigidity, and severe itching, the application and development of jute fiber in the field of clothing fabrics has been restricted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A blended yarn of jute, polyester and nylon fibers, which is prepared by blending jute, polyester and nylon fibers as raw materials; in terms of raw material weight percentage, jute accounts for 42.5% of the entire weight ratio; polyester accounts for the entire weight 26.5% of the ratio; nylon accounts for 31% of the entire weight ratio.

[0022] Utilize above-mentioned blended yarn to produce the blended fabric of jute and terylene and nylon fiber, its manufacturing process method comprises the steps:

[0023] 1. Material selection: select yarns with a fineness of 15-40 lbs that are blended with 42.5% jute, 26.5% polyester and 31% nylon as raw materials.

[0024] 2, sizing: adopt sizing liquid to carry out sizing to the raw material selected in step 1, this sizing liquid is the mixed liquid of PVA size liquid, grafted starch and polyacrylamide pulp, wherein, the weight ratio of PVA size liquid and grafted starch is 1: 2; The weight ratio of the mixture of PVA slurry ...

Embodiment 2

[0032] A blended yarn of jute, polyester and nylon fibers, which is prepared by blending jute, polyester and nylon fibers as raw materials; in terms of raw material weight percentage, jute accounts for 50% of the entire weight ratio; polyester accounts for the entire weight Ratio of 28%; Nylon accounted for 22% of the entire weight ratio.

[0033] Utilize above-mentioned blended yarn to produce the blended fabric of jute and terylene and nylon fiber, its manufacturing process method comprises the steps:

[0034] 1. Material selection: select yarns with a fineness of 15-40 lbs that are blended with 50% jute, 28% polyester and 22% nylon as raw materials.

[0035] 2, sizing: adopt sizing liquid to carry out sizing to the raw material selected in step 1, this sizing liquid is the mixed liquid of PVA size liquid, grafted starch and polyacrylamide pulp, wherein, the weight ratio of PVA size liquid and grafted starch is 1: 1; The weight ratio of the mixture of PVA slurry and grafted...

Embodiment 3

[0043] A blended yarn of jute, polyester and nylon fibers, which is prepared by blending jute, polyester and nylon fibers as raw materials; in terms of raw material weight percentage, jute accounts for 30% of the entire weight ratio; polyester accounts for the entire weight 20% of the ratio; nylon accounts for 50% of the entire weight ratio.

[0044]Utilize above-mentioned blended yarn to produce the blended fabric of jute and terylene and nylon fiber, its manufacturing process method comprises the steps:

[0045] 1. Material selection: Select yarns with a fineness of 15-40 English counts blended with 30% jute, 20% polyester and 50% nylon as raw materials.

[0046] 2, sizing: adopt sizing liquid to carry out sizing to the raw material selected in step 1, this sizing liquid is the mixed liquid of PVA size liquid, grafted starch and polyacrylamide pulp, wherein, the weight ratio of PVA size liquid and grafted starch is 1: 4; The weight ratio of the mixture of PVA slurry and gra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a blended yarn of a jute fiber, a polyester fiber and a nylon fiber. The blended yarn is made by blending the following raw materials in percentage by weight: 30 to 50 percent of jute fiber, 20 to 30 percent of polyester and 20 to 50 percent of nylon. By blending the jute fiber, the polyester fiber and the nylon fiber in a reasonable proportion, the blended yarn overcomes the shortcomings that the jute fabric is rough and hard and easy to drape, and has the advantages of moisture absorption, air permeability, antibacterium, high strength, wear resistance and the like of the jute fabric. Blended fabric made of the blended yarn is suitable for making coats, sportswear and the like.

Description

technical field [0001] The invention belongs to the field of textiles, and in particular relates to a blended yarn of jute, polyester and nylon fibers and an application thereof. Background technique [0002] As the prices of raw materials such as cotton fiber and chemical fiber continue to rise, people begin to demand other fibers that can replace chemical fiber and cotton. Among them, hemp fiber, especially jute fiber, is cheap, and my country has abundant jute resources, ranking third in the world. The development and application of jute fiber has attracted more and more people's attention in the country where big jute is grown. The planting of jute fiber does not occupy fertile land, does not require a large amount of chemical fertilizers, and does not require too much manual management, and jute has better moisture absorption and release properties than ramie and flax, and its anti-mildew and antibacterial ability is also stronger in hemp fibers, such as The ability to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D06M15/11D06M15/333D06M15/285D06M16/00C12S11/00D06M15/643D06M15/53D06L3/02D06L4/12D06L4/13
Inventor 刘国忠张熙明蒋建新
Owner JIANGSU REDBUD DYEING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap