High-speed tool steel for drill bit

A high-speed tool steel and high-speed steel technology, applied in the field of alloy steel, can solve the problems of low tool life and narrow quenching temperature range, and achieve the effects of wide quenching temperature range, uniform carbide distribution, and grain refinement.

Inactive Publication Date: 2012-06-20
朱昌宏 +1
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, M2 steel also has other disadvantages, such as narrow quenching temperature range (1200-1220 ℃), and the service life of the tool is relatively low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-speed tool steel for drill bit
  • High-speed tool steel for drill bit
  • High-speed tool steel for drill bit

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high-speed tool steel for drill bits, its components are C, W, Mo, Cr, V, Mn, Si, Nb, Co, P, S and Fe, and the weight percentage of each component is C: 0.92%; W: 5.30%; Mo: 4.60%; Cr: 4.70%; V: 1.80%; Mn: 0.25%; Si: 0.20%; Nb: 0.08%; Co: 1.32%; P: ≤0.02%; S: ≤0.007%; The sum of copper and nickel content does not exceed 0.25%; the rest is Fe.

[0019] The organization performance of this embodiment is shown in Table 1:

[0020] Table 1

[0021]

Embodiment 2

[0023] A high-speed tool steel for drill bits, the chemical composition of which is C, W, Mo, Cr, V, Mn, Si, Nb, Co, P, S and Fe, and the weight percentage of the composition range is C: 0.90%; W: 5.00% ; Mo: 4.50%; Cr: 4.55%; V: 1.90%; Mn: 0.25%; Si: 0.29%; Nb: 0.28%; Co: 1.30%; P: ≤0.03%; S: ≤0.007%; copper and The sum of nickel content does not exceed 0.25%; the rest is Fe.

[0024] The organization performance of this embodiment is shown in Table 2:

[0025] Table 2

[0026]

Embodiment 3

[0028] A high-speed tool steel for drill bits, the chemical composition of which is C, W, Mo, Cr, V, Mn, Si, Nb, Co, P, S and Fe, and the weight percentage of the composition range is C: 0.91%; W: 5.60% Mo: 4.50%; Cr: 4.91%; V: 1.85%; Mn: 0.30%; Si: 0.27%; Nb: 0.30%; Co: 1.50%; P: ≤0.03%; S: ≤0.02%; copper and The sum of nickel content does not exceed 0.25%; the rest is Fe.

[0029] The organization performance of this embodiment is shown in Table 3:

[0030] table 3

[0031]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
crystal sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-speed tool steel for drill bits, which comprises the following components: 0.90-0.98% of C; 5.00-5.80% of W; 4.00-4.60% of Mo; 3,80-5.00% of Cr; 1.80-2.20% of V; 0.25-0.45% of Mn; 0.2-0.40% of Si; 0.08-0.30% of Nb; 1.30-1.60% of Co; not more than 0.03% of P; not more than 0.03% of S; and the balance of Fe. According to the invention, the using amounts of precious metal tungsten and molybdenum are reduced; a little niobium is added; the steel is provided with good application performance and processing performance; and prepared cutters have increased service life.

Description

Technical field [0001] The invention relates to an alloy steel, which is a high-speed tool steel for drill bits, and belongs to the technical field of metallurgy. Background technique [0002] High-speed steel is high-carbon high-alloy ledeburite steel, which contains a large amount of alloy carbides. High-speed steel has high hardness, good wear resistance, toughness and red hardness after proper heat treatment. The main purpose of high-speed steel is to manufacture machine tool cutting tools, high-end molds, high-temperature bearings, and mechanical parts that require high hardness and good wear resistance. It is widely used. [0003] The main alloying elements of high-speed steel are tungsten, molybdenum, chromium and vanadium, etc., which are all carbide forming elements. Their reserves on the earth are limited. Among them, tungsten and molybdenum reserves are less, precious and scarce, which are national strategic materials. Must be used sparingly. However, the content of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/30
Inventor 朱昌宏蒋慧娟
Owner 朱昌宏
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap