Preparation method for halogen-free flame retardant polyester labeled paper

A flame-retardant polyester and label paper technology, applied in chemical instruments and methods, papermaking, paper, etc., can solve the problems of reducing the initial viscosity and stickiness of pressure-sensitive adhesives, difficult to ensure pressure-sensitivity, and affecting product appearance, etc. Achieve the effect of enhancing pressure-sensitive adhesive performance, excellent pressure-sensitive adhesive pressure-sensitive adhesive performance, eliminating environmental pollution and harm to human body

Active Publication Date: 2012-06-27
SICHUAN DONGFANG INSULATING MATERIAL
View PDF7 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Chinese patent application number 200980101125.0 and publication number CN102131640A provide a "flame retardant multilayer label", which includes a first layer containing a polymer matrix and a flame retardant - a top coat, a second layer - a base film and a second layer Three layers - an acrylic adhesive layer containing a flame retardant, the three layers work together to make a VTM-0 level (a burning level of a thin material in the US UL laboratory standard) halogen-free flame-retardant labels, of which the top coating Both the flame retardant in the layer and the adhesive layer use ammonium polyphosphate, which has a good flame retardant effect, but ammonium polyphosphate is an externally added inorganic solid flame retardant. First, the solid flame retardant is combined with the liquid adhesive or the top layer The compatibility of the paint is not good, which affects the appearance of the product. In addition, the addition of flame retardants mixed with acrylic pressure-sensitive adhesives reduces the initial viscosity and persistent viscosity of the pressure-sensitive adhesives. It is difficult to ensure its flame retardancy. Ensure that its pressure sensitivity meets the requirements
At the same time, the base film does not use flame-retardant materials, and it is difficult to make the overall flame-retardant grade of the label reach VTM-0 only by adding a flame-retardant top coat and adhesive layer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for halogen-free flame retardant polyester labeled paper
  • Preparation method for halogen-free flame retardant polyester labeled paper
  • Preparation method for halogen-free flame retardant polyester labeled paper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] 1. Preparation of phosphorus-containing flame retardant acrylic prepolymer resin:

[0036] At room temperature, 20Kg of butyl acrylate, 45Kg of isooctyl acrylate, 3Kg of acrylic acid, 2Kg of hydroxyethyl acrylate, 10Kg of ethyl methacrylate, 20Kg of phosphorus-containing flame retardant monomer (2-allylphenoxy) pentaphenoxy Base ring triphosphazene, 100Kg of solvent (ethyl acetate:toluene=19:1), and 0.5Kg of benzoyl peroxide were added to the reaction kettle with condensation reflux device, so that the temperature of the condenser was controlled below 15 ℃, and the number of revolutions Stir at 200 rpm and mix evenly; gradually heat up to 80° C. under nitrogen protection, carry out solution copolymerization reaction for 4 hours, stop heating, and the reaction ends.

[0037] Another: add 100Kg of ethyl acetate and mix evenly, cool to room temperature and discharge to prepare phosphorus-containing acrylic prepolymer resin (A), so that the solid content reaches 33% for lat...

Embodiment 2

[0043] 1. Preparation of phosphorus-containing flame retardant acrylic prepolymer resin:

[0044] Mix 50Kg butyl acrylate, 15Kg isooctyl acrylate, 3Kg acrylic acid, 2Kg hydroxyethyl acrylate, 10Kg ethyl methacrylate, 20Kg phosphorus-containing flame retardant monomer allyl diethyl phosphate, 100Kg solvent (ethyl acetate) at room temperature Ester:toluene=19:1), 0.5Kg of benzoyl peroxide were added to the reaction kettle with condensation reflux device, so that the temperature of the condenser was controlled below 15 ℃, stirred at 200 rpm, and mixed uniformly; gradually under nitrogen protection The temperature was raised to 80° C., the solution copolymerization reaction was carried out for 4 h, the heating was stopped, and the reaction was completed.

[0045] Another: Add 100Kg of ethyl acetate and mix evenly, cool to room temperature and discharge to prepare phosphorus-containing acrylic prepolymer resin (B), so that the solid content reaches 33% for later use.

[0046] 2. P...

Embodiment 3

[0051] 1. Preparation of phosphorus-containing flame retardant acrylic prepolymer resin:

[0052] At room temperature, 30Kg of butyl acrylate, 40Kg of isooctyl acrylate, 6Kg of acrylic acid, 4Kg of hydroxyethyl acrylate, 10Kg of ethyl methacrylate, 10Kg of phosphorus-containing flame retardant monomer (2-allylphenoxy) pentaphenoxy Cyclotriphosphazene, 100Kg of solvent (ethyl acetate:toluene=19:1), and 1.0Kg of azobisisobutyl cyanide were added to the reaction kettle with a condensation reflux device, so that the temperature of the condenser was controlled below 15 ℃, so that the Stir at 200 rpm and mix evenly; gradually heat up to 80° C. under nitrogen protection, carry out solution copolymerization reaction for 4 h, stop heating, and the reaction ends.

[0053] Another: add 100Kg of ethyl acetate to mix evenly, cool to room temperature and discharge to prepare phosphorus-containing acrylic prepolymer resin (C), so that the solid content reaches 33% for later use.

[0054] 2....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for halogen-free flame retardant polyester labeled paper. The method is characterized in that the method comprises the following steps: adopting butyl acrylate, ethylhexyl acrylate, acrylic acid, hydroxyethyl acrylate, ethyl methacrylate, a phosphorus-containing flame retardant monomer, a solvent, an initiator, and the like as raw materials to prepare a phosphorus-containing flame retardant acrylic acid pre-polymerization resin; preparing a phosphorus-containing flame retardant acrylic acid pressure sensitive adhesive; uniformly coating the phosphorus-containing flame retardant acrylic acid pressure sensitive adhesive on a halogen-free flame retardant polyester thin film; compounding the polyacrylate pressure sensitive adhesive-coated halogen-free flame retardant polyester thin film and a polyester release film; and carrying out ripening to prepare the halogen-free flame retardant polyester label product. With the present invention, the flame retardant and pressure sensitive adhesion property, the appearance and the environmental protection quality of the whole label product can be effectively improved, and the halogen-free flame retardant polyester labeled paper can meet the performance requirement of VTM-0 grade flame retardation.

Description

technical field [0001] The invention belongs to a layered product-a preparation method of label paper, and relates to a preparation method of halogen-free flame-retardant polyester label paper. The label paper product prepared by the invention is suitable for product labels in places with specific requirements such as flame-retardant, fire-resistant and high-temperature resistant electrical appliances, household appliances, batteries, and transportation. Background technique [0002] At present, most of the label papers used in electronic appliances, home appliances, batteries and transportation industries are made of plastic film as the base material and coated with self-adhesive materials. Among them, polyester film is widely used as the base material of electronic and electrical labels due to its excellent water, oil, chemical resistance, insulation and certain high temperature resistance. Acrylic pressure-sensitive adhesive has the characteristics of good low temperatur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/38D21H21/14D21H19/16D21H19/20C08F220/18C08F230/02C09J133/08C09J11/08C09J11/06B32B27/36B32B7/12G09F3/02
Inventor 刘洪乐丁俊
Owner SICHUAN DONGFANG INSULATING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap